Abstract: The invention relates to a method for coating a substrate according to which a self-crosslinking coating composition is produced on the basis of a) at least one hydrolysable silane with at least one nonhydrolysable substituent, said silane having one or more electrophilic groups X on at least one nonhydrolysable substitutent, b) at least one hydrolysable silane with at least one nonhydrolysable substituent, said silane having one or more nucleophilic groups Y on at least one nonhydrolysable substituent, c) at least one hydrolysable silane with at least one nonhydrolysable carbonic group that has an average of 2 to 30 fluorine atoms that are bound to one or more aliphatic carbon atoms that are separated from the silicon atom by at least two atoms.

Abstract: A ceramic composite material with a density of >90% of the theoretical density based on SiC and carbon, with a silicon carbide content of between 99.9% by weight and 70% by weight and a carbon content of between 0.

Abstract: Magnetic particles with an outer glass surface being essentially poreless or having pores of a diameter of less then 10 nm as well as ferromagnetic particles with a glass surface are preferentially useful for the isolation of biological material from samples. They provide a quick and reliable purification.

Abstract: Magnetic glass particles are prepared containing a magnetic core coated with a glass layer having a substantially pore-free glass surface. The particles are used for separating biological material such as nucleic acids. A preferred process of preparing the particles is by forming a mixture of magnetic cores with a sol formed from an alcohol and a metal alkoxide, spray-drying the mixture to coat the cores with a layer of gelled sol, and heating the coated cores to obtain the magnetic glass particles. Preferably, the particles have an average particle size of less than 100 &mgr;m and any pores of the glass surface have a diameter of less than 10 nm. The magnetic core may be a composite material containing a mica core and magnetite particles immobilized on the mica core, and the glass layer may contain boron oxide. Magnetic core materials include magnetite (Fe3O4) and Fe2O3.

Abstract: A process for preparing an agglomerate-free suspension of nanosize iron-containing oxide particles coated in a stable manner comprises preparing an aqueous suspension of nanosize iron-containing oxide particles which are partially or completely in the form of agglomerates; adding a trialkoxysilane and a water-miscible polar organic solvent which has a boiling point at least 10° C. higher than the boiling point of water; treating the resulting suspension with ultrasound until at least 70% of the particles present are in the range of ±20% of the average particle diameter; removing the water by distillation under the action of ultrasound; and separating the non-disintegrated agglomerates.

Abstract: The invention is directed to a method for producing low sintering fine-particle multicomponent glass powder having a particle size of the primary particle in the nanometer range. The method utilizes microemulsion techniques with subsequent separation of the particles out of the emulsion and calcination for utilization as glass flow having a sintering temperature <900.degree. C. or in a glass flow, for generating thin transparent layers or for generating color decorations on glass, glass ceramic or ceramic substrates after adding a coloring pigment to the glass flow. The microemulsion for producing the nanoscale glass powder particles is generated from a nonionic ambiphilic emulsifier with a component of 10 to 15 percent by weight on the emulsion, from an oil phase having a portion of 50 to 70 percent by weight and a glass precursor-containing aqueous salt solution having a portion of up to 31.3 percent by weight with salt contents of up to 45 percent by weight.