Abstract: The fibrillation tendency of solvent-spun cellulose fiber is reduced by treating the previously dried fiber with a chemical reagent containing at least two functional groups which are reactive with cellulose and which are electrophilic carbon--carbon double bonds, particularly vinyl sulfone groups, or precursors thereof or electrophilic three-membered heterocyclic rings or precursors thereof. The chemical reagent is preferably colorless and is preferably applied to the fiber from aqueous solution. The fiber may be contained in a woven or knotted fabric.

Abstract: The present invention relates to a method for reducing the fibrillation tendency of lyocell fibre. Never-dried fibre is treated by an inorganic alkali solution and a chemical reagent having an average of greater than 2.1 acrylamido groups, and then heated. This method produces cellulose materials with a smooth white appearance resistant to creasing in the wet state.

Abstract: The fibrillation tendency of lyocell fabrics, and the degree of fibrillation of fibrillated lyocell fabrics, can be reduced by treating such fabrics with a cross-linking agent in the presence of an acid catalyst. Good results may be obtained when the ratio by weight of the catalyst to the optional cross-linking agent is at least about 0.5:1. Good results may be obtained when the amount of cross-linking agent fixed on the fabric is in the range 0.5 to 1.5 percent on weight of fabric.