Abstract: The present invention provides a method of producing grain oriented electrical steel having excellent mechanical and magnetic properties. A hot processed strip having a thickness of 1.5-4.0 mm thickness a composition consisting essentially of 2.5-4.5% silicon, 0.1-1.2% chromium, less than 0.050% carbon, less than 0.005% aluminum, up to 0.1% sulfur, up to 0.14% selenium, 0.01-1% manganese and balance being essentially iron and residual elements, all percentages by weight. The strip has a volume resistivity of at least 45 .mu..OMEGA.-cm, at least 0.010% carbon so that an austenite volume fraction (.gamma..sub.1150.degree. C.) of at least 2.5% is present in the hot processed strip and each surface of the strip has an isomorphic layer having a thickness of at least 10% of the total thickness of the hot processed strip. The strip is cold reduced to an intermediate thickness, annealed, cold reduced to a final thickness and decarburized to less than 0.003% carbon.