Abstract: This disclosure provides an investigation of the kinetic uptake properties of water in amorphous PEF and PET across the entire water activity interval at various temperatures, and also investigates the corresponding equilibrium uptake properties at the same conditions. Uptake data were measured using three independent and complementary methodologies, and excellent agreement was observed among all three methodologies. Accordingly, this disclosure provides for methods of plasticizing poly(ethylene furanoate) film by cold water sorption, and provides a plasticized poly(ethylene furanoate) (PEF) film made according to the disclosed methods. Methods for making thin films of PEF are also provided.

Abstract: This disclosure provides an investigation of the kinetic uptake properties of water in amorphous PEF and PET across the entire water activity interval at various temperatures, and also investigates the corresponding equilibrium uptake properties at the same conditions. Uptake data were measured using three independent and complementary methodologies, and excellent agreement was observed among all three methodologies. Accordingly, this disclosure provides for methods of plasticizing poly(ethylene furanoate) film by cold water sorption, and provides a plasticized poly(ethylene furanoate) (PEF) film made according to the disclosed methods. Methods for making thin films of PEF are also provided.

Abstract: The present invention relates to improved methods for measuring the renewable bio-source carbon content and renewable bio-content in renewable bioplastic resins produced in manufacturing plants. In particular, the present invention relates to measuring the renewable bio-source carbon content in renewable bioplastic resins produced during a production run by correlating measured ?13C values are measured by iTOC-CRDS and CM-CRDS with actual renewable bio-source carbon content measurements (AMS or LSC 14C) via a linear regression.

Abstract: The present invention relates to improved methods for measuring the renewable bio-source carbon content and renewable bio-content in renewable bioplastic resins produced in manufacturing plants. In particular, the present invention relates to measuring the renewable bio-source carbon content in renewable bioplastic resins produced during a production run by correlating measured ?13C values are measured by iTOC-CRDS and CM-CRDS with actual renewable bio-source carbon content measurements (AMS or LSC14C) via a linear regression.