Abstract: A method for manufacturing a metal graphite brush comprises steps of preparing natural graphite powders of 60-70 wt %, electrolytic copper powders of 30-40 wt %, molybdenum disulfide and lead of 2.5 wt % and the mixed resin of novolak phenol resin and furfural resin powders of 1-15 wt % which are adhesives, wet-mixing graphite powders with adhesives, pulverizing mixed powders to diameters of less than 200 .mu.m, press-molding all the powders under a pressure of 2-3 ton/cm.sup.2 and heating at a temperature 700.degree. C., and attaching a lead wire thereto, simultaneously, wherein the average particle distribution of the powders is 27 .mu.m. The compound ratio of graphite powders: copper powders: molybdenum disulfide: lead is 62.5 wt %: 35 wt %: 1.5 wt %: 1.0 wt %, the adhesives comprising the mixed resin of novolak phenol resin and furfural resin by 50:50 is added by a weight ratio of 7.5 wt % to the graphite powders.