Abstract: Disclosed is a continuous preparation method of cellulose fibers, in which a forming tension of 0.1 to 1.9 cN/dtex is applied to a fine solution stream obtained by extrusion through a spinneret plate and air gap cooling, then the fine solution stream is fed into a coagulating bath at a speed of 80 to 1000 m/min, a traction tension of 0.075 to 1.5 cN/dtex is continued to be applied to washed fibers in a water washing system behind the coagulating bath, and finally, the washed fibers are fed into a post-treatment system for continuous and efficient spinning of finished fibers at a speed of 80 to 1000 m/min.

Abstract: The present disclosure discloses a method for preparing cellulose fiber. The method includes the following steps: 1) mixing cellulose pulp with NMMO aqueous solution of a mass concentration of 60%-85%, preferably 70% to 76%, to obtain a uniform mixture; 2) subjecting the obtained uniform mixture to dewatering for swelling, dissolution, and deaerating to obtain a cellulose spinning stock solution; 3) the cellulose spinning stock solution entering into a spinning machine after being filtered and heat exchange, and entering into a coagulation system after carrying out extruding by a spinneret-pack and cooling by air, and then coagulating in a NMMO coagulating bath of a mass concentration of 50% to 72% to obtain nascent fiber; and 4) subjecting the nascent fiber to rinsing to obtain a fiber filament bundle, and then, performing subsequent-section treatment to obtain cellulose fiber.

Abstract: The present invention provides a process for preparing a cellulose solution. NMMO with a relatively low concentration and non-activated pulp are continuously mixed online, the mixed premix is dewatered in evaporation dewatering equipment until an NMMO concentration suitable for swelling is achieved, then, sufficient swelling is carried out under this condition, and the uniformly-mixed and sufficiently swelled pre-swelling solution is subjected to depressurized evaporation dewatering and dissolving by thin-film-evaporation equipment thereby obtaining a high-concentration, uniformly-dissolved and excellently-uniformity cellulose solution. The present invention further provides continuous preparation equipment for the process for preparing a cellulose solution.

Abstract: The present disclosure discloses a method for preparing cellulose fiber. The method includes the following steps: 1) mixing cellulose pulp with NMMO aqueous solution of a mass concentration of 60%-85%, preferably 70% to 76%, to obtain a uniform mixture; 2) subjecting the obtained uniform mixture to dewatering for swelling, dissolution, and deaerating to obtain a cellulose spinning stock solution; 3) the cellulose spinning stock solution entering into a spinning machine after being filtered and heat exchange, and entering into a coagulation system after carrying out extruding by a spinneret-pack and cooling by air, and then coagulating in a NMMO coagulating bath of a mass concentration of 50% to 72% to obtain nascent fiber; and 4) subjecting the nascent fiber to rinsing to obtain a fiber filament bundle, and then, performing subsequent-section treatment to obtain cellulose fiber.

Abstract: The present invention provides a process for preparing a cellulose solution. NMMO with a relatively low concentration and non-activated pulp are continuously mixed online, the mixed premix is dewatered in evaporation dewatering equipment until an NMMO concentration suitable for swelling is achieved, then, sufficient swelling is carried out under this condition, and the uniformly-mixed and sufficiently swelled pre-swelling solution is subjected to depressurized evaporation dewatering and dissolving by thin-film-evaporation equipment thereby obtaining a high-concentration, uniformly-dissolved and excellently-uniformity cellulose solution. The present invention further provides continuous preparation equipment for the process for preparing a cellulose solution.