Abstract: A composition including from: a) 35% to 100% by weight of at least one semicrystalline aliphatic polyamide and/or one polyamide of formula MXDZ wherein MXD is meta-xylylenediamine and Z is a C6 to C12 aliphatic dicarboxylic acid, the semicrystalline aliphatic polyamide and/or the polyamide of formula MXDZ having a total acidity between from 70 to 180 ?eq/g and a total basicity of less than 100 ?eq/g; b) 0 to 25% by weight of polyolefins; c) 0 to 60% by weight, of glass fibers; d) 0 to 2% by weight of at least one additive; e) 0 to 30% by weight of at least one flame retardant; the sum a)+b)+c)+d)+e) being equal to 100%, the semicrystalline aliphatic polyamide and/or the polyamide of formula MXDZ having a melt flow index (MFI) between from 4 to 50 g/10 min.

Abstract: A mixture of solid and hollow glass reinforcers with an alloy of at least one polyamide and of at least one polyolefin, the mixture of solid and hollow glass reinforcers including from 5% to 60% by weight of hollow glass beads relative to the sum of the solid and hollow glass reinforcers, the alloy-mixture proportions being from more than 50% to 75% of said mixture of solid and hollow glass reinforcers, to prepare a composition having a modulus, when dry at 20° C., of from 5 GPa to less than 8 GPa as measured according to ASTM D-2520-13, at a frequency of at least 1 GHz, at 23° C., under 50% RH.

Abstract: The present invention relates to the use of a mixture of at least one semi-crystalline aliphatic polyamide and at least one amorphous polyamide, wherein the at least one semi-crystalline aliphatic polyamide is obtained by polycondensation: of at least one C6 to C18, preferentially C10 to C18, more preferentially C10 to C12 amino acid, or at least one C6 to C18, preferentially C10 to C18, more preferentially C10 to C12 lactam, or at least one C4-C36, preferentially C5-C18, preferentially C5-C12, more preferentially C10-C12 diamine Ca, with at least one C4-C36, preferentially C6-C18, preferentially C6-C12, more preferentially C10-C12 dicarboxylic acid Cb; in order to prepare a semi-crystalline composition, the modulus of which does not vary by more than 25% within the temperature range from 10° C. to 40° C.

Abstract: The use of a mixture of solid and hollow glass reinforcements with an alloy of at least one polyamide and at least one polyolefin, the mixture of solid and hollow glass reinforcements including from 5 to 50% by weight of hollow glass beads relative to the total of solid and hollow glass reinforcements for the dry preparation at 23° C. of a composition having a modulus at least equal to 8 GPa and a dielectric constant Dk less than or equal to 3.5 as measured according to ASTM D-2520-13, at a frequency of at least 1 GHz, at 23° C., under 50% RH.