Abstract: A mixture made from or containing T1) from 99 wt % to 75 wt % of bitumen, and T2) from 1 wt % to 25 wt % of a polymer composition made from or containing A) 5-35% by weight of a propylene homopolymer; B) 20-50% by weight of an ethylene homopolymer; and C) 30-60% by weight of a terpolymer of ethylene, propylene, and 1-butene.

Abstract: Asphalt product made from or containing Z1) from 90 wt % to 98 wt % of mineral aggregate; and Z2) from 2 wt % to 10 wt % of a bitumen composition made from or containing T1) from 99 wt % to 75 wt % of bitumen, and T2) from 1 wt % to 25 wt % of a polymer composition made from or containing A) 5-35% by weight of a propylene homopolymer; B) 20-50% by weight of an ethylene homopolymer; and C) 30-60% by weight of a terpolymer of ethylene, propylene and 1-butene derived units.

Abstract: A polypropylene composition made from or containing: T1) 35-65 wt % of a recycled polypropylene mixture containing at least 80 wt % of rigid polypropylene items and having a purity of at least 90 wt %; T2) 20-50 wt % of an ethylene/propylene copolymer; T3) 5-20 wt % of a propylene/ethylene heterophasic copolymer composition made from or containing a) from 12 wt % to 52 wt % of a propylene homopolymer or a propylene/ethylene copolymer; and b) from 48 wt % to 88 wt % of a propylene/ethylene copolymer having a content of ethylene derived units ranging from 15 wt % to 42 wt %; wherein the propylene composition has a melt flow rate (ISO 1133 230° C./2.16 kg) ranging from 0.5 to 20 g/10 min.

Abstract: A propylene/1-hexene copolymer having i) the content of 1-hexene derived units, measured by C13-NMR, ranging from 1.5 wt % to 2.5 wt % and the content of propylene derived units ranging from 97.5 to 98.5 wt. %; ii) a melting temperature, measured by DSC, ranging from 148 to 153° C.; iii) an amount of fraction insoluble in xylene at 25° C. higher than 97.0%; and iv) a melt flow rate (MFR), measured according to ISO 1133, 230° C., 2.16 kg, ranging from 35 to 65 g/10 min.

Abstract: A multilayer film made from or containing at least one core layer made from or containing a polypropylene composition made from or containing: A) from 95 wt % to 60 wt %; of a propylene homopolymer having a fraction insoluble in xylene at 25° C. greater than 90 wt %, based upon the total weight of the propylene homopolymer; and B) from 5 wt % to 40 wt %; of an heterophasic propylene ethylene copolymer, the sum of the amounts of A) and B) being 100.

Abstract: An injection molded article made from or containing a propylene-based composition made from or containing: T1) from 90 wt % to 50 wt % of a propylene homopolymer; and T2) from 10 wt % to 50 wt % of a polymer composition made from or containing A) 5-35% by weight of a propylene homopolymer or a propylene ethylene copolymer; B) 20-50% by weight of a copolymer of ethylene and a C3-C8 alpha-olefin containing from 0.1% to 20% by weight of alpha-olefin units; and C) 30-60% by weight of a copolymer of ethylene and propylene containing from 25% to 75% by weight of ethylene units.

Abstract: A process for preparing fibers made from or containing propylene homopolymer having: a melting point ranging from 150° C. to 164° C.; a fraction soluble in xylene at 25° C. between 6.0 wt % and 2.0 wt %; a fraction soluble in acetone 25° C. between 0.5 wt % and 2.0 wt %; a ratio fraction soluble in xylene at 25° C./fraction soluble in acetone 25° C. between 0.30 and 0.60; a polydispersity index ranging from 2.8 to 4.5; and a melt flow rate (ISO 1133, 230° C./2.16 kg) between 2 to 40 g/10 min.

Abstract: A heat-shrinkable label made from or containing a terpolymer film containing propylene, ethylene and 1-hexene, wherein the terpolymer has: (i) a content of ethylene derived units ranging from 0.5 wt % to 5.0 wt %, (ii) a content of 1-hexene derived units ranging from 1.0 wt % to 6.0 wt %, (iii) a melt flow rate (MFR) (ISO 1133 230° C., 2.16 kg) ranging from 0.5 to 20 g/10 min, and (iv) a polydispersity index (P.I.) ranging from 2.0 to 7.0.

Abstract: A propylene polymer composition made from or containing: a) from 15 wt % to 35 wt % of a propylene 1-hexene copolymer containing from 6.2 to 8.5% by weight, of 1-hexene derived units and having a Melt Flow Rate from 3.5 to 8.5 g/10 min; b) from 15 wt % to 35 wt % of a propylene 1-hexene copolymer containing from 10.4 wt % to 14.5 wt %, of 1-hexene derived units and having a Melt Flow Rate from 3.5 to 8.5 g/10 min; and c) from 38 wt % to 68 wt % of a propylene ethylene copolymer containing from 3.4 wt % to 5.7 wt % of ethylene derived units and having a Melt Flow Rate from 3.5 to 12.0 g/10 min, wherein the sum of the amount of a), b) and c) being 100.

Abstract: A fiber of a propylene ethylene copolymer having: i) xylene soluble fraction at 25° C. ranging from 14 wt % to 27 wt %; ii) intrinsic viscosity of the fraction soluble in xylene at 25° C. ranging from 1.0 to 2.4 dl/g; iii) melt flow rate, MFR, ranging from 12 g/10 min to 60 g/10 min; iv) an ethylene derived units content ranging from 5.0 wt % to 12.0 wt %; v) the ethylene derived units content of the fraction insoluble in xylene at 25° C. ranging from 2.5 wt % to 6.0 wt %; vi) the ethylene derived units content of the fraction soluble in xylene at 25° C. ranging from 15.2. wt % to 30.2 wt % vii) C13 NMR sequences PEP measured on the fraction insoluble in xylene at 25° C. ranging from 3.5 mol % to 5.5 mol %; and viii) the C13 NMR sequences PEP measured on the fraction soluble in xylene at 25° C. ranging from 11.0 mol % to 14.2 mol %.

Abstract: A multilayer film made from or containing a core layer made from or containing a polypropylene composition made from or containing: A) from 90 wt % to 50 wt %; of a propylene homopolymer; and B) from 10 wt % to 50 wt %; of a propylene ethylene copolymer having: i) xylene soluble fraction at 25° C. ranging from 14 wt % to 27 wt %; ii) intrinsic viscosity of the fraction soluble in xylene at 25° C. ranging from 1.0 to 2.4 dl/g; iii) melt flow rate ranging from 1.0 g/10 min to 4.0 g/10 min; iv) an ethylene content ranging from 5.0 wt % to 12.0 wt %; v) the ethylene derived units content on the fraction insoluble in xylene at 25° C. ranging from 2.5 wt % to 6.0 wt %; vi) the ethylene derived units content on the fraction soluble in xylene at 25° C. ranging from 15.2. wt % to 30.2 wt %, the sum of A) and B) being 100 wt %.

Abstract: A polyolefin composition made from or containing: T1) 50-90 wt % of a recycled polyolefin mixture and T2) 10-50 wt % of a polyolefin component, containing A) 5-35% by weight of a propylene homopolymer or a propylene ethylene copolymer; B) 20-50% by weight of an ethylene homopolymer; and C) 30-60% by weight of a terpolymer of ethylene, propylene, and 1-butene made from or containing 45 to 65 percent by weight of ethylene units and from 15 to 38 percent by weight of 1-butene units.

Abstract: A polyolefin composition made from or containing: T1) 50-90 wt % of a recycled polyolefin mixture; and T2) 10-50 wt % of a polyolefin component containing: A) 5-35% by weight of a propylene homopolymer or a propylene ethylene copolymer; B) 20-50% by weight of a copolymer of ethylene and a C3-C8 alpha-olefin made from or containing 0.1-20% by weight of alpha-olefin units; and C) 30-60% by weight of a copolymer of ethylene and propylene made from or containing 25-75% by weight of ethylene units.

Abstract: A polyolefin composition made from or containing: A) 5-35% by weight of a propylene homopolymer; B) 20-50% by weight of an ethylene homopolymer; and C) 30-60% by weight of a terpolymer of ethylene, propylene and 1-butene derived units.

Abstract: A polyolefin composition made from or containing: A) 5-35% by weight of a propylene ethylene copolymer; B) 20-50% by weight of an ethylene homopolymer; and C) 30-60% by weight of a terpolymer of ethylene, propylene and 1-butene derived units.

Abstract: A mixture made from or containing T1) from 99 wt % to 75 wt % of bitumen, and T2) from 1 wt % to 25 wt % of a polymer composition made from or containing A) 5-35% by weight of a propylene homopolymer or a propylene ethylene copolymer; B) 20-50% by weight of a copolymer of ethylene and a C3-C8 alpha-olefin containing from 1.0% to 20.0% by weight of alpha-olefin units; and C) 30-60% by weight of a copolymer of ethylene and propylene containing from 25.0% to 75.0% by weight of ethylene derived units.

Abstract: A process for the preparation of a propylene polymer containing a coloring agent in an amount ranging from 0.2 to 30 ppm referred to the weight of propylene polymer, including the steps of: a) providing a solid ZN catalyst component made from or containing Mg, Ti, halogen and an internal electron donor compound, wherein the Ti being in an amount ranging from 0.1 to 10% of the total weight of solid catalyst component; b) providing a coloring agent made from or containing at least a pigment; c) mixing the ZN catalyst particles and the coloring agent in a liquid hydrocarbon medium, thereby obtaining a slurry and d) feeding the slurry to a polymerization reactor and subjecting the reactor to polymerization conditions, thereby yielding the propylene polymer.

Abstract: A terpolymer compositions made from or containing: A) From 80 wt % to 97 wt %; of a first propylene, ethylene, 1-butene terpolymer having: i) the content of ethylene derived units ranging from 0.5 wt % to 3.2 wt %; ii) the content of 1-butene derived units ranging from 7.2 wt % to 14.8 wt %; and B) From 20 wt % to 3 wt %; of a second propylene, ethylene, 1-butene terpolymer having: i) the content of ethylene derived units ranging from 0.5 wt % to 3.2 wt %; ii) the content of 1-butene derived units ranging from 14.4 wt % to 26.5 wt %; and the terpolymer composition having the melt flow rate, MFR, measured according to ISO 1133 at 230° C. with a load of 2.16 kg, ranging from 3.0 g/10 min to 20.0 g/10 min; the sum of the amounts of A) and B) being 100 wt %.

Abstract: A propylene ethylene copolymer having: i) xylene soluble fraction at 25° C. ranging from 14 wt % to 27 wt %; ii) intrinsic viscosity of the fraction soluble in xylene at 25° C. ranging from 1.0 to 2.4 dl/g; iii) melt flow rate, MFR, ranging from 1.0 g/10 min to 50.0 g/10 min; iv) an ethylene derived units content ranging from 5.0 wt % to 12.0 wt %; v) the ethylene derived units content on the fraction insoluble in xylene at 25° C. ranging from 2.5 wt % to 6.0 wt %; vi) the ethylene derived units content on the fraction soluble in xylene at 25° C. ranging from 15.2. wt % to 30.2 wt %; and vii) C13 NMR sequences PEP measured on the fraction insoluble in xylene at 25° C. ranging from 3.5 mol % to 5.5 mol % and C13 NMR sequences PEP measured on the fraction soluble in xylene at 25° C. ranging from 11.0 mol % to 14.2 mol %.

Abstract: A polyolefin composition made from or containing: T1) 70-95 wt %, of a polyolefin component containing: a1) from 30 wt % to 70 wt % of a propylene based polymer; and a2) from 30 wt % to 70 wt % of an ethylene based polymer; and T2) 5-30 wt % of a polyolefin component containing: A) 5-35% by weight of a propylene homopolymer or a propylene ethylene copolymer; B) 25-50% by weight of a copolymer of ethylene and a C3-C8 alpha-olefin containing 0.1-20% by weight of C3-C8 alpha-olefin units; and C) 30-60% by weight of a copolymer of ethylene and propylene containing 25-75% by weight of ethylene units.