Abstract: A method for forming a quaternary alloy film of Co—W—P—Au for use as a diffusion barrier layer on a copper interconnect in a semiconductor structure and devices formed incorporating such film are disclosed. In the method, a substrate that has copper conductive regions on top is first pre-treated by two separate pre-treatment steps. In the first step, the substrate is immersed in a H2SO4 rinsing solution and next in a solution containing palladium ions for a length of time sufficient for the ions to deposit on the surface of the copper conductive regions. The substrate is then immersed in a solution that contains at least 15 gr/l sodium citrate or EDTA for removing excess palladium ions from the surface of the copper conductive regions.

Abstract: A method for forming a quaternary alloy film of Co—W—P—Au for use as a diffusion barrier layer on a copper interconnect in a semiconductor structure and devices formed incorporating such film are disclosed. In the method, a substrate that has copper conductive regions on top is first pre-treated by two separate pre-treatment steps. In the first step, the substrate is immersed in a H2SO4 rinsing solution and next in a solution containing palladium ions for a length of time sufficient for the ions to deposit on the surface of the copper conductive regions. The substrate is then immersed in a solution that contains at least 15 gr/l sodium citrate or EDTA for removing excess palladium ions from the surface of the copper conductive regions.

Abstract: A method for forming a quaternary alloy film of Co—W—P—Au for use as a diffusion barrier layer on a copper interconnect in a semiconductor structure and devices formed incorporating such film are disclosed. In the method, a substrate that has copper conductive regions on top is first pre-treated by two separate pre-treatment steps. In the first step, the substrate is immersed in a H2SO4 rinsing solution and next in a solution containing palladium ions for a length of time sufficient for the ions to deposit on the surface of the copper conductive regions. The substrate is then immersed in a solution that contains at least 15 gr/l sodium citrate or EDTA for removing excess palladium ions from the surface of the copper conductive regions.