Abstract: The invention relates to a method for preparing titanium alloys based on aluminothermic self-propagating gradient reduction and slag-washing refining, and belongs to the technical field of titanium-aluminum alloys. The method comprises the following steps of pre-treating raw materials, weighing the raw materials in the mass ratio of rutile or high-titanium slags or titanium dioxide to aluminum powder to V2O5 powder to CaO to KClO3 being 1.0:(0.60-0.24):(0.042-0.048):(0.12-0.26):(0.22-0.30), performing an aluminothermic self-propagating reaction in a gradient feeding manner to obtain high-temperature melt, performing a gradient reduction melting, performing heat insulation and separating the melt after the feeding is completed, then adding CaF2—CaO—TiO2—V2O5 based refining slags into the high-temperature melt, performing slag washing refining, and finally removing slags to obtain titanium alloys.

Abstract: Provided is a method for preparing a reduced titanium powder by a multistage deep reduction, including the following steps of: uniformly mixing a dried titanium dioxide powder with a magnesium powder to obtain a mixture, adding the mixture in a self-propagating reaction furnace, triggering a self-propagating reaction, obtaining an intermediate product of which low-valence titanium oxides TixO are dispersed in an MgO matrix, leaching the intermediate product with a hydrochloric acid as a leaching solution, performing filtering, washing and vacuum drying to obtain a low-valence titanium oxide TixO precursor, uniformly mixing the low-valence titanium oxide TixO precursor with a calcium powder, performing a pressing to obtain semi-finished products, placing the semi-finished products in a vacuum reduction furnace for a second-time deep reduction, and leaching a deep reduction product with a hydrochloric acid as a leaching solution so as to obtain the reduced titanium powder.

Abstract: Provided is a method for preparing a reduced titanium powder by a multistage deep reduction, including the following steps of: uniformly mixing a dried titanium dioxide powder with a magnesium powder to obtain a mixture, adding the mixture in a self-propagating reaction furnace, triggering a self-propagating reaction, obtaining an intermediate product of which low-valence titanium oxides TixO are dispersed in an MgO matrix, leaching the intermediate product with a hydrochloric acid as a leaching solution, performing filtering, washing and vacuum drying to obtain a low-valence titanium oxide TixO precursor, uniformly mixing the low-valence titanium oxide TixO precursor with a calcium powder, performing a pressing to obtain semi-finished products, placing the semi-finished products in a vacuum reduction furnace for a second-time deep reduction, and leaching a deep reduction product with a hydrochloric acid as a leaching solution so as to obtain the reduced titanium powder.

Abstract: The invention relates to a method for preparing titanium alloys based on aluminothermic self-propagating gradient reduction and slag-washing refining, and belongs to the technical field of titanium-aluminum alloys. The method comprises the following steps of pre-treating raw materials, weighing the raw materials in the mass ratio of rutile or high-titanium slags or titanium dioxide to aluminum powder to V2O5 powder to CaO to KClO3 being 1.0:(0.60-0.24):(0.042-0.048):(0.12-0.26):(0.22-0.30), performing an aluminothermic self-propagating reaction in a gradient feeding manner to obtain high-temperature melt, performing a gradient reduction melting, performing heat insulation and separating the melt after the feeding is completed, then adding CaF2—CaO—TiO2—V2O5 based refining slags into the high-temperature melt, performing slag washing refining, and finally removing slags to obtain titanium alloys.