Abstract: Provided is a process for preparing a molybdenum alloy by ultra-high-temperature rolling. The molybdenum alloy is an ultra-high strength and toughness molybdenum alloy, and includes 95 wt % to 99.9 wt % of molybdenum and 0.1 wt % to 5 wt % of a nano-ceramic oxide particle. The process includes: (1) preparing an MOx—SO3H aqueous solution; (2) preparing a precursor composite powder; (3) preparing a nano-ceramic oxide-reinforced molybdenum alloy powder by reduction; and (4) preparing the ultra-high strength and toughness molybdenum alloy by pressing and sintering.

Abstract: The present application relates to polyurea/calcium sulfonate complex grease composition for use in constant velocity joints. The invention discloses a lubricating grease with thixotropy and a preparation method thereof. The lubricating grease comprises a polyurea/high base number calcium sulfonate composite thickener, colloidally dispersed calcium carbonate solid particles in the form of calcite, a calcium borate or calcium borate composite, a calcium soap of fatty acid having 12 to 24 carbon atoms, an organic molybdenum compound, and an antioxidant. The above components are uniformly dispersed in an oil phase medium. The content of high base number calcium sulfonate in the lubricating grease is less than 22 wt %.

Abstract: A method of reinforcing a metallic material includes adding graphene to an alcohol solution; subjecting the alcohol solution containing graphene to sonication; mixing a metal powder with the alcohol solution containing graphene; milling the metal powder and alcohol solution containing graphene mixture; drying the metal powder and alcohol solution containing graphene mixture to form a composite powder; subjecting the composite powder to a densification process followed by a hot isostatic pressing treatment to form a composite material; and molding the composite material by hot extrusion.

Abstract: A method for preparing a graphene/metal composite sheet includes adding polyvinyl alcohol into distilled water and heat to about 100° C. under stirring to prepare a polyvinyl alcohol solution; dispersing graphene in distilled water using ultrasonication to prepare a graphene solution; mixing the polyvinyl alcohol solution and the graphene solution to form a graphene/polyvinyl alcohol mixed slurry; after a metal sheet is subjected to a surface activation treatment, coating the graphene/polyvinyl alcohol mixed slurry onto the metal sheet at both upper and lower surfaces; vacuum sintering to remove the polyvinyl alcohol in the surface coating to obtain a graphene/metal plate; overlaying at least two graphene/metal plates and bonding them together via hot isostatic pressing to form multilayer graphene/metal plates; and hot rolling the bonded multilayer graphene/metal plates to form the graphene/metal composite sheet.

Abstract: A method of reinforcing a metallic material includes adding graphene to an alcohol solution; subjecting the alcohol solution containing graphene to sonication; mixing a metal powder with the alcohol solution containing graphene; milling the metal powder and alcohol solution containing graphene mixture; drying the metal powder and alcohol solution containing graphene mixture to form a composite powder; subjecting the composite powder to a densification process followed by a hot isostatic pressing treatment to form a composite material; and molding the composite material by hot extrusion.

Abstract: A method for preparing a graphene/metal composite sheet includes adding polyvinyl alcohol into distilled water and heat to about 100° C. under stirring to prepare a polyvinyl alcohol solution; dispersing graphene in distilled water using ultrasonication to prepare a graphene solution; mixing the polyvinyl alcohol solution and the graphene solution to form a graphene/polyvinyl alcohol mixed slurry; after a metal sheet is subjected to a surface activation treatment, coating the graphene/polyvinyl alcohol mixed slurry onto the metal sheet at both upper and lower surfaces; vacuum sintering to remove the polyvinyl alcohol in the surface coating to obtain a graphene/metal plate; overlaying at least two graphene/metal plates and bonding them together via hot isostatic pressing to form multilayer graphene/metal plates; and hot rolling the bonded multilayer graphene/metal plates to form the graphene/metal composite sheet.