Abstract: A hot-rolled steel sheet having a tensile strength greater than 800 MPa and an elongation at break greater than 10% is provided. A composition of the steel includes, the contents being expressed by weight: 0.050%?C?0.090%, 1%?Mn?2%, 0.015%?Al?0.050%, 0.1%?Si?0.3%, 0.10%?Mo?0.40%, S?0.010%, P?0.025%, 0.003%?N?0.009%, 0.12%?V?0.22%, Ti?0.005%, Nb?0.020% and optionally, Cr?0.45%. A balance of the composition includes iron and inevitable impurities resulting from the smelting. A microstructure of the sheet or part includes, as a surface fraction, at least 80% upper bainite, and a remainder includes lower bainite, martensite and residual austenite. A sum of the martensite and residual austenite, as a surface fraction, is less than 5%.

Abstract: The invention relates to a hot-rolled steel sheet having a tensile strength greater than 800 MPa and an elongation at break greater than 10%, the composition of which comprises, the contents being expressed by weight: 0.050%?C?0.090%, 1%?Mn?2%, 0.015%?Al?0.050%, 0.1%?Si?0.3%, 0.10%?Mo?0.40%, S?0.010%, P?0.025%, 0.003%?N?0.009%, 0.12%?V?0.22%, Ti?0.005%, Nb?0.020% and, optionally, Cr?0.45%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, the microstructure of the sheet or the part comprising, as a surface fraction, at least 80% upper bainite, the possible complement consisting of lower bainite, martensite and residual austenite, the sum of the martensite and residual austenite contents being less than 5%.

Abstract: The invention relates to a hot-rolled steel sheet having a tensile strength greater than 800 MPa and an elongation at break greater than 10%, the composition of which comprises, the contents being expressed by weight: 0.050%?C?0.090%, 1%?Mn?2%, 0.015%?Al?0.050%, 0.1%?Si?0.3%, 0.10%?Mo?0.40%, S?0.010%, P?0.025%, 0.003%?N?0.009%, 0.12%?V?0.22%, Ti?0.005%, Nb?0.020% and, optionally, Cr?0.45%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, the microstructure of the sheet or the part comprising, as a surface fraction, at least 80% upper bainite, the possible complement consisting of lower bainite, martensite and residual austenite, the sum of the martensite and residual austenite contents being less than 5%.

Abstract: A hot-rolled steel sheet having a tensile strength greater than 800 MPa and an elongation at break greater than 10% is provided. A composition of the steel includes, the contents being expressed by weight: 0.050%?C?0.090%, 1%?Mn?2%, 0.015%?Al?0.050%, 0.1%?Si?0.3%, 0.10%?Mo?0.40%, S?0.010%, P?0.025%, 0.003%?N?0.009%, 0.12%?V?0.22%, Ti?0.005%, Nb?0.020% and optionally, Cr?0.45%. A balance of the composition includes iron and inevitable impurities resulting from the smelting. A microstructure of the sheet or part includes, as a surface fraction, at least 80% upper bainite, and a remainder includes lower bainite, martensite and residual austenite. A sum of the martensite and residual austenite, as a surface fraction, is less than 5%.

Abstract: The invention relates to a hot-rolled steel sheet having a tensile strength greater than 800 MPa and an elongation at break greater than 10%, the composition of which comprises, the contents being expressed by weight: 0.050%?C?0.090%, 1%?Mn?2%, 0.015%?Al?0.050%, 0.1%?Si?0.3%, 0.10%?Mo?0.40%, S?0.010%, P?0.025%, 0.003%?N?0.009%, 0.12%?V?0.22%, Ti?0.005%, Nb?0.020% and, optionally, Cr?0.45%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, the microstructure of the sheet or the part comprising, as a surface fraction, at least 80% upper bainite, the possible complement consisting of lower bainite, martensite and residual austenite, the sum of the martensite and residual austenite contents being less than 5%.

Abstract: The invention relates to a hot-rolled steel sheet having a tensile strength greater than 800 MPa and an elongation at break greater than 10%, the composition of which comprises, the contents being expressed by weight: 0.050%?C?0.090%, 1%?Mn?2%, 0.015%?Al?0.050%, 0.1%?Si?0.3%, 0.10%?Mo?0.40%, S?0.010%, P?0.025%, 0.003%?N?0.009%, 0.12%?V?0.22%, Ti?0.005%, Nb?0.020% and, optionally, Cr?0.45%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, the microstructure of the sheet or the part comprising, as a surface fraction, at least 80% upper bainite, the possible complement consisting of lower bainite, martensite and residual austenite, the sum of the martensite and residual austenite contents being less than 5%.