Abstract: The present invention provides a method for preparing an antibacterial and low-adhesion cross-linked polyvinyl alcohol coating. A simple two-step method is adopted, wherein polyfunctional isocyanate is first used to strongly cross-link with the hydroxyl group of polyvinyl alcohol, and then a compound with low surface energy such as mono-hydroxyl silicone oil or the like is received in to effectively reduce the surface energy of the surface of the coating; and two structure-function relationships are efficiently synergistic through effective strong cross-linking and regulation of the compound with low surface energy within the system, enabling the strongly cross-linked polyethylene coating to have excellent performance of water adhesion resistance and oil adhesion resistance, and good performance of bacterial adhesion resistance, which is expected to be applied in the fields of materials for antifouling and self-cleaning, liquid transportation and implantation in animal body.

Abstract: The disclosure relates to a field of functional coating technologies, and particularly to a durable inorganic super-hydrophilic paint, a preparation method and an application thereof. The durable inorganic super-hydrophilic paint includes the following preparation raw materials in percentage by mass: 30˜60% silicate, 5˜25% zinc oxide, 10˜40% water and 0.1˜5% wetting agent. The coating formed by a durable inorganic super-hydrophilic paint prepared by the method is a flat rigid coating, with good appearance, excellent antifouling self-cleaning and anti-microbial adhesion properties, long-term underwater stability and high mechanical strength. The paint may be applied to building external walls and home inner walls for its antifouling self-cleaning property and may be applied to a field of oil field and oil-water separation for its excellent underwater oleophobic property.

Abstract: The invention discloses an anti-fouling polyurethane thin film with high elasticity and high transparency, a preparation method and use thereof. The raw materials of the polyurethane thin film include the following active ingredients by mass fractions: 30% to 40% of a hard segment monomer, 40% to 50% of a soft segment monomer, 3% to 6% of a hydrophilic monomer, 0% to 3% of a crosslinking monomer, 0% to 5% of a small molecular chain extender, and 10% to 15% of a compound with low surface energy. A chemically and physically double-crosslinked anti-fouling polyurethane is synthesized through a polycondensation reaction. This thin film exhibits superior low adhesion and anti-fouling properties, and can achieve the coexistence of both low adhesion and stretchability at the same time.