Abstract: A hydrogen-free amorphous dielectric insulating film having a high material density and a low density of tunneling states. The film is prepared by deposition of a dielectric material on a substrate having a high substrate temperature Tsub under high vacuum and at a controlled low deposition rate. In one embodiment, the film is amorphous silicon while in another embodiment the film is amorphous germanium.

Abstract: A hydrogen-free amorphous dielectric insulating film having a high material density and a low density of tunneling states. The film is prepared by deposition of a dielectric material on a substrate having a high substrate temperature Tsub under high vacuum and at a controlled low deposition rate. In one embodiment, the film is amorphous silicon while in another embodiment the film is amorphous germanium.

Abstract: A process for forming a doped nc-Si thin film thermoelectric material. A nc-Si thin film is slowly deposited on a substrate, either by hot-wire CVD (HWCVD) with a controlled H2:SiH4 ratio R=6-10 or by plasma-enhanced (PECVD) with a controlled R=80-100, followed by ion implantation of an n- or p-type dopant and a final annealing step to activate the implanted dopants and to remove amorphous regions. A doped nc-Si thin film thermoelectric material so formed has both a controllable grain size of from a few tens of nm to 3 nm and a controllable dopant distribution and thus can be configured to provide a thermoelectric material having predetermined desired thermal and/or electrical properties. A final annealing step is used to activate the dopants and remove any residual amorphous regions.

Abstract: A hydrogen-free amorphous dielectric insulating film having a high material density and a low density of tunneling states is provided. The film is prepared by e-beam deposition of a dielectric material on a substrate having a high substrate temperature Tsub under high vacuum and at a low deposition rate. In an exemplary embodiment, the film is amorphous silicon having a density greater than about 2.18 g/cm3 and a hydrogen content of less than about 0.1%, prepared by e-beam deposition at a rate of about 0.1 nm/sec on a substrate having Tsub=400° C. under a vacuum pressure of 1×10?8 Torr.

Abstract: A process for forming a doped nc-Si thin film thermoelectric material. A nc-Si thin film is slowly deposited on a substrate, either by hot-wire CVD (HWCVD) with a controlled H2:SiH4 ratio R=6-10 or by plasma-enhanced (PECVD) with a controlled R=80-100, followed by ion implantation of an n- or p-type dopant and a final annealing step to activate the implanted dopants and to remove amorphous regions. A doped nc-Si thin film thermoelectric material so formed has both a controllable grain size of from a few tens of nm to 3 nm and a controllable dopant distribution and thus can be configured to provide a thermoelectric material having predetermined desired thermal and/or electrical properties. A final annealing step is used to activate the dopants and remove any residual amorphous regions.

Abstract: A process for forming a doped nc-Si thin film thermoelectric material. A nc-Si thin film is slowly deposited on a substrate, either by hot-wire CVD (HWCVD) with a controlled H2:SiH4 ratio R=6-10 or by plasma-enhanced (PECVD) with a controlled R=80-100, followed by ion implantation of an n- or p-type dopant and a final annealing step to activate the implanted dopants and to remove amorphous regions. A doped nc-Si thin film thermoelectric material so formed has both a controllable grain size of from a few tens of nm to 3 nm and a controllable dopant distribution and thus can be configured to provide a thermoelectric material having predetermined desired thermal and/or electrical properties. A final annealing step is used to activate the dopants and remove any residual amorphous regions.

Abstract: A process for forming a doped nc-Si thin film thermoelectric material. A nc-Si thin film is slowly deposited on a substrate, either by hot-wire CVD (HWCVD) with a controlled H2:SiH4 ratio R=6-10 or by plasma-enhanced (PECVD) with a controlled R=80-100, followed by ion implantation of an n- or p-type dopant and a final annealing step to activate the implanted dopants and to remove amorphous regions. A doped nc-Si thin film thermoelectric material so formed has both a controllable grain size of from a few tens of nm to 3 nm and a controllable dopant distribution and thus can be configured to provide a thermoelectric material having predetermined desired thermal and/or electrical properties. A final annealing step is used to activate the dopants and remove any residual amorphous regions.

Abstract: A hydrogen-free amorphous dielectric insulating film having a high material density and a low density of tunneling states is provided. The film is prepared by e-beam deposition of a dielectric material on a substrate having a high substrate temperature Tsub under high vacuum and at a low deposition rate. In an exemplary embodiment, the film is amorphous silicon having a density greater than about 2.18 g/cm3 and a hydrogen content of less than about 0.1%, prepared by e-beam deposition at a rate of about 0.1 nm/sec on a substrate having Tsub=400° C. under a vacuum pressure of 1×10?8 Torr.