Abstract: A method for the manufacture of a composite fragmenting material having exothermic properties includes the steps of packing a mold with preformed metal fragments; filling interstitial spaces surrounding the metal fragments with a reactive metal powder to form a mixture; and then sintering the mixture at a temperature effective to both coat the metal fragments with the reactive metal powder and to bond the metal fragments together. In one embodiment the composite fragmenting material is formed into a nosecone for a warhead.

Abstract: A composition includes an alloy that has, by weight, 25-65% zirconium, 25-65% tungsten, and 6-25% of a combined amount of nickel in at least one of iron and cobalt. The alloy may be formed into a geometric body that has a density of 7.8 grams per cubic centimeter to 11.4 grams per cubic centimeter.

Abstract: A method for the manufacture of a composite fragmenting material having exothermic properties includes the steps of packing a mold with preformed metal fragments; filling interstitial spaces surrounding the metal fragments with a reactive metal powder to form a mixture; and then sintering the mixture at a temperature effective to both coat the metal fragments with the reactive metal powder and to bond the metal fragments together. In one embodiment the composite fragmenting material is formed into a nosecone for a warhead.

Abstract: The subject invention reveals a process for making hardened powder metal parts which comprises compacting a powder metal composition into a green preformed metal part and subsequently sintering said green metal part to produce the powder metal part at an elevated temperature and subsequently cooling the sintered part at a rate which is sufficient to insure the formation of a substantial amount of martensite, wherein the powder metal composition is comprised of copper powder, a nickel powder and a base iron powder wherein said composition contains from about 1 weight percent to about 5 weight percent of the total sum of said copper powder and said nickel powder and wherein the ratio of the nickel powder to the copper powder is within the range of 1:1 to 9:1, and wherein the balance of said composition constitutes iron.