Abstract: A cerium-zirconium based mixed oxide composition have: (a) a Ce:Zr molar ratio of 1 or less, and (b) a cerium oxide content of 10-50% by weight. The composition has (i) a surface area of at least 18 m2/g, and a total pore volume as measured by N2 physisorption of at least 0.11 cm3/g, after ageing at 1100° C. in an air atmosphere for 6 hours, (ii) a surface area of at least 42 m2/g, and a total pore volume as measured by N2 physisorption of at least 0.31 cm3/g, after ageing at 1000° C. in an air atmosphere for 4 hours, and (iii) Dynamic Oxygen Storage Capacity (D-OSC) value as measured by H2-TIR of greater than 500 ?mol/g at 600° C. after aging at 800° C. in an air atmosphere for 2 hours. A process contacts the exhaust gas with the composition Another process is for preparing the composition.

Abstract: This invention relates to an aqueous dispersion of particles, the dispersion having a particle content of 10-70 wt %, and the particles comprising, on an oxide basis: (a) 10-98 wt % in total of ZrO2+HfO2, and (b) 2-90 wt % in total of AI2O3, CeO2, La2O3, Nd2O3, Pr6O11, Y2O3, or a transition metal oxide, wherein the dispersion has a Z-average particle size of 100-350 nm and the particles have a crystallite size of 1-9 nm. The invention also relates to a substrate coated with the aqueous dispersion of particles.

Abstract: A passive NOX adsorbent includes: palladium, platinum or a mixture thereof and a mixed or composite oxide including the following elements in percentage by weight, expressed in terms of oxide: 10-90% by weight zirconium and 0.1-50% by weight of least one of the following: a transition metal or a lanthanide series element other than Ce. Although the passive NOX adsorbent can include Ce in an amount ranging from 0.1 to 20% by weight expressed in terms of oxide, advantages are obtained particularly in the case of low-Ce or a substantially Ce-free passive NOx adsorbent.

Abstract: A passive NOX adsorbent includes: palladium, platinum or a mixture thereof and a mixed or composite oxide including the following elements in percentage by weight, expressed in terms of oxide: 10-90% by weight zirconium and 0.1-50% by weight of least one of the following: a transition metal or a lanthanide series element other than Ce. Although the passive NOX adsorbent can include Ce in an amount ranging from 0.1 to 20% by weight expressed in terms of oxide, advantages are obtained particularly in the case of low-Ce or a substantially Ce-free passive NOx adsorbent.

Abstract: This invention relates to a zirconium solution or sol comprising: (a) zirconium, (b) nitrate, acetate and/or chloride ions, and (c) one or more complexing agents being an organic compound comprising at least one of the following functional groups: an amine, an organosulphate, a sulphonate, a hydroxyl, an ether or a carboxylic acid group, wherein the molar ratio of components (a):(b) is 1:0.7 to 1:4.0, the molar ratio of components (a):(c) is 1:0.0005 to 1:0.1, and the pH of the zirconium solution or sol is less than 5.

Abstract: A passive NOX adsorbent includes: palladium, platinum or a mixture thereof and a mixed or composite oxide including the following elements in percentage by weight, expressed in terms of oxide: 10-90% by weight zirconium and 0.1-50% by weight of least one of the following: a transition metal or a lanthanide series element other than Ce. Although the passive NOX adsorbent can include Ce in an amount ranging from 0.1 to 20% by weight expressed in terms of oxide, advantages are obtained particularly in the case of low-Ce or a substantially Ce-free passive NOx adsorbent.

Abstract: This invention relates to azirconium solution or sol comprising: (a) zirconium, (b) nitrate, acetate and/or chloride ions, and (c) one or more complexing agents being an organic compound comprising at least one of the following functional groups: an amine, an organosulphate, a sulphonate, a hydroxyl, an ether or a carboxylic acid group, wherein the molar ratio of components (a):(b) is 1:0.7 to 1:4.0, the molar ratio of components (a):(c) is 1:0.0005 to 1:0.1, and the pH of the zirconium solution or sol is less than 5.

Abstract: This invention relates to a cerium-zirconium based mixed oxide having: (a) a Ce:Zr molar ratio of 1 or less, and (b) a cerium oxide content of 10-50% by weight, wherein the composition has (i) a surface area of at least 18 m2/g, and a total pore volume as measured by N2 physisorption of at least 0.11 cm3/g, after ageing at 1100° C. in an air atmosphere for 6 hours, and (ii) a surface area of at least 42 m2/g, and a total pore volume as measured by N2 physisorption of at least 0.31 cm3/g, after ageing at 1000° C. in an air atmosphere for 4 hours. The invention also relates to a catalytic system comprising the cerium-zirconium based mixed oxide, as well as to a process 10 for treating an exhaust gas from a vehicle engine comprising contacting the exhaust gas with the cerium-zirconium based mixed oxide.