Abstract: A metal fiber based on one or several elements from the group of platinum, palladium, rhodium, ruthenium, and iridium with 0 to 30% by weight of one or several additional alloy elements from the group of nickel, cobalt, gold, rhenium, molybdenum, and tungsten, contains 1 to 500 ppm by weight of boron or phosphorus. A non-woven material or netting, in particular for the production of nitrogen oxide or for the production of hydrocyanic acid, is made of such fibers. For the production of fibers based on noble metals having up to 30% by weight of additional alloy metals by drawing the fibers from a melt, the melting point of the metal is reduced by at least 400° C., before drawing of the fibers, by additionally alloying with boron or phosphorus, and the boron or the phosphorus is removed again from the fibers.

Abstract: Methods are known for producing a body from a material susceptible to thermal cracking, in particular from an alloy, by casting a melt of the material in a mold with thermally insulated side walls and a bottom of material with good thermal conducting properties and cooling the melt in the casting mold, where the solid-liquid interface forming as the border between the melt and the already solidified material essentially extends parallel to the bottom and, in the course of the solidification of the melt, moves from the bottom in the direction of the exposed surface of the melt.

Abstract: Catalytic gauzes which have an enlarged surface can be manufactured from a wire made of 90Pt/10Rh, for example, by coating the wire with a base metal, thermally treating the wire under partial conversion of the 90Pt/10Rh into solid solutions with the base metal, dissolving the base metal and weaving a wire gauze. They are used for the oxidation of ammonia and the ammoxidation of methane.

Abstract: A rod made of a hard material is inserted into a pipe made of a relatively soft material, and a two-element arrangement having an intermediate size is obtained by hot-rolling and drawing. In these steps, the cross section is reduced by at least 50%. Subsequently, another pipe of the soft material is fitted onto the two-element arrangement, and the so-obtained three-element arrangement is adjusted to its final size by means of hot or cold rolling followed by cold drawing.