Abstract: Embodiments of the present disclosure are directed to multilayer structures. The multilayer structures may include a first layer and a barrier layer. The first layer may include, based on the total weight of the first layer, from 90 wt. % to 99.5 wt. % of an ethylene/alpha-olefin interpolymer having a density of from 0.945 g/cc to 0.970 g/cc and from 0.5 wt. % to 10 wt. % of a compatibilizer. The compatibilizer may include an anhydride and/or carboxylic acid functionalized ethylene/alpha-olefin elastomer having a density of from 0.850 g/cc to 0.910 g/cc and a melt viscosity of greater than 200,000 cP, when measured at 177 C.

Abstract: Embodiments of the present disclosure are directed to multilayer structures. The multilayer structures may include a first layer and a barrier layer. The first layer may include, based on the total weight of the first layer, from 90 wt. % to 99.5 wt. % of an ethylene/alpha-olefin interpolymer having a density of from 0.945 g/cc to 0.970 g/cc and from 0.5 wt. % to 10 wt. % of a compatibilizer. The compatibilizer may include an anhydride and/or carboxylic acid functionalized ethylene/alpha-olefin elastomer having a density of from 0.850 g/cc to 0.910 g/cc and a melt viscosity of greater than 200,000 cP, when measured at 177 C.

Abstract: Provided is a method for increasing the melt strength and/or low shear viscosity of a polyethylene resin. The method includes: a) providing a polyethylene composition including the reaction product of ethylene and optionally, one or more alpha-olefin comonomers, wherein the polyethylene composition is characterized by the following properties: a density ranging from 0.900 g/cm3 to 0.970 g/cm3, a molecular weight distribution (Mw/Mn) ranging from 2.6 to 3.5, and from 0.10 to 0.27 vinyl groups per 1,000 total carbon atoms; b) providing a masterbatch composition including a free radical generator and a polyethylene resin, wherein the free radical generator has a half-life at 220° C. of less than 200 seconds, and a decomposition energy higher than ?250 kJ/mol, and wherein the polyethylene resin has a density ranging from 0.900 g/cm3 to 0.970 g/cm3, melt index ranging from 0.

Abstract: A method for increasing the melt strength and/or low shear viscosity of a polyethylene resin, the method comprising a) providing a polyethylene composition comprising the reaction product of ethylene and optionally, one or more alpha-olefin comonomers, wherein the polyethylene composition is characterized by the following properties: a density ranging from 0.900 g/cm3 to 0.970 g/cm3, a molecular weight distribution (Mw/Mn) ranging from 2.6 to 3.5, and from 0.10 to 0.27 vinyl groups per 1,000 total carbon atoms; b) providing a masterbatch composition comprising a free radical generator and a polyethylene resin, wherein the free radical generator has a half-life at 220 C of less than 200 seconds, and a decomposition energy higher than ?250 kJ/mol, and wherein the polyethylene resin has a density ranging from 0.900 g/cm3 to 0.970 g/cm3, melt index ranging from 0.01 g/10 min to 100 g/10 min; and c) reacting the polyethylene composition with the masterbatch composition to form a modified polyethylene composition.