Abstract: Batteries with particularly high energy capacity and low internal impedance have been described herein. The batteries can exhibit extraordinary long cycling with acceptable low amounts of fade. Pouch batteries using high specific capacity lithium rich metal oxide as positive electrode material combined with graphitic carbon anode can reach an energy density of at least about 180 Wh/kg at a rate of C/3 from 4.35V to 2V at room temperature while having a room temperature areas specific DC resistance of no more than about 75 ohms-cm2 at 20% SOC based on a full charge to 4.35V. High specific capacity lithium rich metal oxide with specific stoichiometry ranges used in these batteries are disclosed.

Abstract: Batteries with particularly high energy capacity and low internal impedance have been described herein. The batteries can exhibit extraordinary long cycling with acceptable low amounts of fade. Pouch batteries using high specific capacity lithium rich metal oxide as positive electrode material combined with graphitic carbon anode can reach an energy density of at least about 180 Wh/kg at a rate of C/3 from 4.35V to 2V at room temperature while having a room temperature areas specific DC resistance of no more than about 75 ohms-cm2 at 20% SOC based on a full charge to 4.35V. High specific capacity lithium rich metal oxide with specific stoichiometry ranges used in these batteries are disclosed.

Abstract: Positive electrode active materials are described that have a high tap density and high specific discharge capacity upon cycling at room temperature and at a moderate discharge rate. Some materials of interest have the formula Li1+xNi?Mn?Co?O2, where x ranges from about 0.05 to about 0.25, ? ranges from about 0.1 to about 0.4, ? ranges from about 0.4 to about 0.65, and ? ranges from about 0.05 to about 0.3. The materials can be coated with a metal fluoride to improve the performance of the materials especially upon cycling. Also, the coated materials can exhibit a very significant decrease in the irreversible capacity lose upon the first charge and discharge of the battery.

Abstract: Positive electrode active materials are described that have a high tap density and high specific discharge capacity upon cycling at room temperature and at a moderate discharge rate. Some materials of interest have the formula Li1+xNi?Mn?Co?O2, where x ranges from about 0.05 to about 0.25, ? ranges from about 0.1 to about 0.4, ? ranges from about 0.4 to about 0.65, and ? ranges from about 0.05 to about 0.3. The materials can be coated with a metal fluoride to improve the performance of the materials especially upon cycling. Also, the coated materials can exhibit a very significant decrease in the irreversible capacity lose upon the first charge and discharge of the battery.