Abstract: The invention discloses an oriented silicon steel with excellent magnetic properties and a manufacturing method thereof. The present invention obtains the oriented silicon steel with excellent magnetic properties by controlling the area ratio of small crystal grains of D<5 mm in an oriented silicon steel finished product to be not more than 3%, and controlling the ratio ?17/?15 of the magnetic conductivity under the magnetic induction of 1.7 T and 1.5 T in the oriented silicon steel finished product to be 0.50 or more.

Abstract: A method for producing a silicon steel normalizing substrate comprises steelmaking, hot rolling and normalizing steps. A normalizing furnace is used in the normalizing step, and along a moving direction of strip steel, the normalizing furnace sequentially comprises: a preheating section, a nonoxidizing heating section, a furnace throat, furnace sections for subsequent normalizing processing, and a delivery seal chamber. Furnace pressures of the normalizing furnace are distributed as follows: the furnace pressure of a downstream furnace section adjacent to the furnace throat along the moving direction of the strip steel is the highest, the furnace pressure decreases gradually from the furnace section with the highest furnace pressure to a furnace section in an inlet direction of the normalizing furnace, and the furnace pressure decreases gradually from the furnace section with the highest furnace pressure to a furnace section in an outlet direction of the normalizing furnace.

Abstract: The invention discloses an oriented silicon steel with excellent magnetic properties and a manufacturing method thereof. The present invention obtains the oriented silicon steel with excellent magnetic properties by controlling the area ratio of small crystal grains of D<5 mm in an oriented silicon steel finished product to be not more than 3%, and controlling the ratio ?17/?15 of the magnetic conductivity under the magnetic induction of 1.7 T and 1.5 T in the oriented silicon steel finished product to be 0.50 or more.

Abstract: A cold-rolling method for preventing fracture of high-silicon strip steel, characterized in that the high-silicon strip steel has a Si content ?2.3 wt %, and at the beginning of cold-rolling, the temperature of inlet strip steel is above 45° C.; during the cold-rolling process, an emulsion liquid is sputtered to the strip steel, a flow rate of the emulsion liquid is 3500 L/min at the inlet in rolling direction, a flow rate of the emulsion liquid is 1500-4000 L/min at an outlet in the rolling direction, and the temperature of the strip steel is maintained above 45° C. under the precondition to guarantee technological lubrication. The cold-rolling method of the invention might prevent fracture of a head portion and a tail portion of the strip steel, raise the rate of finished products, and increase production efficiency.

Abstract: A method for producing a silicon steel normalizing substrate comprises steelmaking, hot rolling and normalizing steps. A normalizing furnace is used in the normalizing step, and along a moving direction of strip steel, the normalizing furnace sequentially comprises: a preheating section, a nonoxidizing heating section, a furnace throat, furnace sections for subsequent normalizing processing, and a delivery seal chamber. Furnace pressures of the normalizing furnace are distributed as follows: the furnace pressure of a downstream furnace section adjacent to the furnace throat along the moving direction of the strip steel is the highest, the furnace pressure decreases gradually from the furnace section with the highest furnace pressure to a furnace section in an inlet direction of the normalizing furnace, and the furnace pressure decreases gradually from the furnace section with the highest furnace pressure to a furnace section in an outlet direction of the normalizing furnace.

Abstract: A method for manufacturing an oriented silicon steel product with high magnetic-flux density comprises the following procedures: 1) smelting and casting, wherein the oriented silicon steel is composed of, by weight, 0.035˜0.065% of C, 2.9˜4.0% of Si, 0.05˜0.20% of Mn, 0.005˜0.01% of S, 0.015˜0.035% of Al, 0.004˜0.009% of N, 0.005˜0.090% of Sn, 0.200˜0.800% of Nb, the rest being Fe; and after being smelted, molten steel is secondarily refined and continuous casted into steel slabs; 2) hot rolling; 3) normalizing; 4) cold rolling; 5) decarburization annealing; 6) MgO coating; 7) high temperature annealing: said sheets are firstly heated to 700˜900° C. and then secondarily heated to 1200° C. at temperature rise rate of 9˜17° C./hr and maintained at 1200° C. for 20 hr; 8) coating an insulation layer.

Abstract: A cold-rolling method for preventing fracture of high-silicon strip steel, characterized in that the high-silicon strip steel has a Si content ?2.3 wt %, and at the beginning of cold-rolling, the temperature of inlet strip steel is above 45° C.; during the cold-rolling process, an emulsion liquid is sputtered to the strip steel, a flow rate of the emulsion liquid is 3500 L/min at the inlet in rolling direction, a flow rate of the emulsion liquid is 1500-4000 L/min at an outlet in the rolling direction, and the temperature of the strip steel is maintained above 45° C. under the precondition to guarantee technological lubrication. The cold-rolling method of the invention might prevent fracture of a head portion and a tail portion of the strip steel, raise the rate of finished products, and increase production efficiency.