Abstract: A method of forming a multilayer coating on a substrate is provided. The multilayer coating exhibits reduced strike-in and mottling. The method includes the steps of providing the substrate including a primer disposed thereon, applying a basecoat composition on the primer, applying a clearcoat composition on the basecoat composition, and curing the basecoat composition and the clearcoat composition to form the multilayer coating on the substrate. The basecoat composition includes a film forming resin, a pigment, and about 5% to about 75% by weight on binder of a cyclic lactone modified branched acrylic polymer having a hydroxyl monomer content of about 1% to 65% by weight, all or part of which has been reacted with a cyclic lactone, and having a weight average molecular weight (Mw) of about 10,000 to about 150,000 g/mol.

Abstract: Sag control compositions, methods of forming sag control compositions, and methods of forming coating systems that include at least one coating layer including urea crystals of such sag control compositions are provided herein. In an embodiment, a sag control composition includes urea crystals and a non-polymeric organic solvent. The urea crystals include the reaction product of a polyisocyanate and a mono-amine. The sag control composition is a stable mixture with a single phase at a temperature of about 21° C. based upon visual observation for a period of at least 10 minutes after forming the mixture.

Abstract: Sag control compositions, methods of forming sag control compositions, and methods of forming coating systems that include at least one coating layer including urea crystals of such sag control compositions are provided herein. In an embodiment, a sag control composition includes urea crystals and a non-polymeric organic solvent. The urea crystals include the reaction product of a polyisocyanate and a mono-amine. The sag control composition is a stable mixture with a single phase at a temperature of about 21° C. based upon visual observation for a period of at least 10 minutes after forming the mixture.

Abstract: The present disclosure is directed to a method of applying at least one layer of a waterborne primer composition, at least one layer of a waterborne basecoat composition and at least one layer of a clearcoat composition to a substrate followed by a heating step which simultaneously cures the applied layers of coating composition.

Abstract: The present disclosure is directed to a method of applying at least one layer of a waterborne primer composition, at least one layer of a waterborne basecoat composition and at least one layer of a clearcoat composition to a substrate followed by a heating step which simultaneously cures the applied layers of coating composition.

Abstract: This invention relates to a method for forming a multi-layer coating on a vehicle body, comprised of applying primer coating, base coating, and clear coat layers in a wet-on-wet-on-wet manner, and simultaneously curing the applied three layers together in a single baking step. The primer layer comprises a film-forming binder comprising two acrylic polymers, the first being a caprolactone-modified branched acrylic polymer and the second being a caprolactone-modified linear acrylic polymer; and a crosslinking agent selected from aminoplast resin, blocked polyisocyanates, or mixtures thereof, wherein the composition is, essentially free of crosslinked nonaqueous dispersion resin particles or crosslinked microgel resin particles or both. The resulting multi-layered coating has excellent aesthetic appearance, strike-in resistance, chipping resistance, sag resistance, and film build even when formed in a three wet layered application method.

Abstract: This invention relates to a method for forming a multi-layer coating, comprising sequentially applying a layer of primer coating composition, a layer of base coat composition, and a layer of clear coat composition on an automotive substrate in a wet-on-wet-on-wet manner, and simultaneously curing the applied three layers together in a single baking step. The primer surfacer comprises a film forming binder, a volatile organic liquid carrier, and pigment(s); and the binder contains about (a) 40 to 95% by weight of a caprolactone-modified highly branched acrylic polymer having a hydroxyl and/or carboxyl monomer content, all or part of which has been reacted with caprolactone, of about 1 to 65% by weight and a weight average molecular weight of about 10,000 to 150,000; and (b) 5 to 60% by weight of an aminoplast resin crosslinking agent. The composition is essentially free of crosslinked nonaqueous dispersion resin particles or crosslinked microgel resin particles or both.