Abstract: The present invention relates to catalysts, more particularly to a cobalt-containing catalyst composition. The present invention further relates to a process for preparing a cobalt-containing catalyst precursor, a process for preparing a cobalt-containing catalyst, and a hydrocarbon synthesis process wherein such a catalyst is used. According to a first aspect of the invention, there is provided a cobalt-containing catalyst composition comprising cobalt and/or a cobalt compound supported on and/or in a silica (SiO2) catalyst support wherein the average pore diameter of the catalyst support is more than 20 nm but less than 50 nm; the catalyst composition also including a titanium compound on and/or in the catalyst support, and a manganese compound on and/or in the catalyst support.

Abstract: The invention provides a process for preparing a cobalt-containing catalyst precursor. The process includes calcining a loaded catalyst support comprising a silica (SiO2) catalyst support supporting cobalt nitrate to convert the cobalt nitrate into cobalt oxide. The calcination includes heating the loaded catalyst support at a high heating rate, which does not fall below 10° C./minute, during at least a temperature range A. The temperature range A is from the lowest temperature at which calcination of the loaded catalyst support begins to 165° C. Gas flow is effected over the loaded catalyst support during at least the temperature range A. The catalyst precursor is reduced to obtain a Fischer-Tropsch catalyst.

Abstract: The present invention relates to catalysts, more particularly to a cobalt-containing catalyst composition. The present invention further relates to a process for preparing a cobalt-containing catalyst precursor, a process for preparing a cobalt-containing catalyst, and a hydrocarbon synthesis process wherein such a catalyst is used. According to a first aspect of the invention, there is provided a cobalt-containing catalyst composition comprising cobalt and/or a cobalt compound supported on and/or in a silica (SiO2) catalyst support wherein the average pore diameter of the catalyst support is more than 20 nm but less than 50 nm; the catalyst composition also including a titanium compound on and/or in the catalyst support, and a manganese compound on and/or in the catalyst support.