Abstract: A toner or a mixture of toners, comprises a pyrogenically synthesized alumina-silica mixed oxide as a component in combination with other components necessary to complete a toner formulation. The surface of the mixed alumina-silica oxide material.

Abstract: A boron oxide-silicon dioxide mixed oxide which has a BET surface of less than 100 m2g, and optionally containing oxides of aluminium, titanium or zirconium, is prepared pyrogenically by flame hydrolysis. The mixed oxide is used in glass making.

Abstract: A toner or a mixture of toners, comprises a pyrogenically synthesized alumina-silica mixed oxide as a component in combination with other components necessary to complete a toner formulation. The surface of the mixed alumina-silica oxide material.

Abstract: A boron oxide-silicon dioxide mixed oxide which has a BET surface of less than 100 m.sup.2 g, and optionally containing oxides of aluminium, titanium or zirconium, is prepared pyrogenically by flame hydrolysis. The mixed oxide is used in glass making.

Abstract: Surface-modified, pyrogenically produced mixed oxides which contain two or more components of the series SiO.sub.2, Al.sub.2 O.sub.3, TiO.sub.2, ZrO.sub.2, Fe.sub.2 O.sub.3, Nb.sub.2 O.sub.5, V.sub.2 O.sub.5, WO.sub.3, SnO.sub.2, GeO.sub.2 and have been surface-modified with one to several compounds of the following groups:(a) organosilanes of the type (RO).sub.3 Si(C.sub.n H.sub.2n+1),(b) R'.sub.x (RO).sub.y Si(C.sub.n H.sub.2n+1),(c) X.sub.3 Si(C.sub.n H.sub.2n+1),(d) X.sub.2 (R')Si(C.sub.n H.sub.2n+1),(e) X(R').sub.2 Si(C.sub.n H.sub.2n+1),(f) (RO).sub.3 Si(CH.sub.2).sub.m --R',(g) (R").sub.x (RO).sub.y Si(CH.sub.2).sub.m --R',(h) X.sub.3 Si(CH.sub.2).sub.m --R',(i) (R)X.sub.2 Si(CH.sub.2).sub.m --R',(j) (R).sub.2 X Si(CH.sub.2).sub.m --R',(k) Silazanes of the type ##STR1## (l) Cyclic polysiloxanes, (m) Polysiloxanes or silicone oils.

Abstract: Pyrogenically produced silica having a specific surface of less than 90 m.sup.2 /g, preferably of less than 60 m.sup.2 /g, and a DBP absorption of less than 60 wt. % (less or equal to 57.30 ml dibutyl phthalate/100 g) is produced by vaporizing silicon halides and/or organosilicon halides, mixing the vapors with a carrier gas, heating the mixture to temperatures definitely above the boiling point of the silicon-halogen compound, mixing with hydrogen and combustion in a known manner in a burner.

Abstract: Granules based on silicon dioxide and having the properties:Average particle size: 10 to 120 .mu.mBET surface area: 40 to 400 m.sup.2 /gPore volume: 0.5 to 2.5 ml/gPore size distribution: less than 5% of the total pore volume exists of pores with a diameter<5 nm, remainder are meso- and macroporespH value: 3.6 to 8.5Tapped density: 220 to 700 g/lThey are prepared by dispersing silicon dioxide in water, spray drying, and optionally heating and/or silanizing. The granules can be used as catalyst supports.

Abstract: Flame-hydrolytically produced titanium dioxide mixed oxide having a BET surface of 10 to 150 m.sup.2 /g and 1 to 30% by weight aluminum oxide or 1 to 30% by weight silicon dioxide is produced by evaporating aluminum chloride or silicon tetrachloride, transferring the evaporated aluminum chloride or silicon tetrachloride, together with an inert gas, into the mixing chamber of a burner, mixing them with hydrogen, air and gaseous titanium tetrachloride, burning the resulting 4-component mixture in the reaction chamber of the burner, and separating the titanium dioxide mixed oxide from the gaseous reaction products.

Abstract: The silanized, pyrogenically prepared silicic acids are prepared by treating pyrogenically prepared silicic acids with an organosilane selected from the group (RO).sub.3 SiC.sub.n H.sub.2n+1, in which n--from 10 to 18 and R stands for an alkyl.

Abstract: Flame-hydrolytically produced titanium dioxide mixed oxide having a BET surface of 10 to 150 m.sup.2 /g and 1 to 30% by weight aluminum oxide or 1 to 30% by weight silicon dioxide is produced by evaporating aluminum chloride or silicon tetrachloride, transferring the evaporated aluminum chloride or silicon tetrachloride, together with an inert gas, into the mixing chamber of a burner, mixing them with hydrogen, air and gaseous titanium tetrachloride, burning the resulting 4-component mixture in the reaction chamber of the burner, and separating the titanium dioxide mixed oxide from the gaseous reaction products.

Abstract: The silanized, pyrogenically prepared silicic acids which are not dispersed in a solvent are prepared by treating pyrogenically prepared silicic acids with an organosilane selected from the group (RO).sub.3 SiC.sub.n H.sub.2n+1, in which n--from 10 to 18 and R stands for an alkyl.

Abstract: Disclosed is an electrophotographic toner comprising a resin, a pigment, and surface-modified, pyrogenically produced aluminum oxide which is has the following physico-chemical properties:______________________________________ Surface (m.sup.2 /g) 50 to 100 Stamping density (g/l) 50 to 90 Drying loss (%) <5 Annealing loss (%) 5.0 to 15 C content (%) 0.5 to 12 pH 4 to 8.

Abstract: Flame-hydrolytically produced titanium dioxide mixed oxide having a BET surface of 10 to 150 m.sup.2 /g and 1 to 30% by weight aluminum oxide or 1 to 30% by weight silicon dioxide is produced by evaporating aluminum chloride or silicon tetrachloride, transferring the evaporated aluminum chloride or silicon tetrachloride, together with an inert gas, into the mixing chamber of a burner, mixing them with hydrogen, air and gaseous titanium tetrachloride, burning the resulting 4-component mixture in the reaction chamber of the burner, and separating the titanium dioxide mixed oxide from the gaseous reaction products.

Abstract: Silicon-aluminum mixed oxide powder which is flamehydrolytically produced and has a composition of 65 to 85% by weight Al.sub.2 O.sub.3, remainder SiO.sub.2 and an amorphous structure, in which each primary particle contains components of SiO.sub.2 and of Al.sub.2 O.sub.3, the primary particles are between 7 and 80 nm, preferably 10 and 40 nm in size and the specific surface of the powder is between 20 and 200 m.sup.2 /g. The powder is used for the production of mullite and sintered compacts manufactured from it.

Abstract: Surface-modified, pyrogenically produced aluminum oxide which is has the following physico-chemical properties:______________________________________ Surface (m.sup.2 /g) 50 to 150 Stamping density (g/l) 50 to 90 Drying loss (%) <5 Annealing loss (%) 5.0 to 15 C content (%) 0.5 to 12 pH 4 to 8.

Abstract: Surface-modified, pyrogenically produced titanium dioxide which has the following physico-chemical properties:______________________________________ Surface (m.sup.2 /g) 5 to 120 Stamping density (g/l) 50 to 250 Drying loss (%) <5 Annealing loss (%) 3.5 to 15 Carbon content (%) 0.5 to 12 pH 4 to 10.

Abstract: Surface-modified, pyrogenically produced aluminum oxide which has the following physico-chemical properties:______________________________________ Surface (m.sup.2 /g) 50 to 150 Stamping density (g/l) 50 to 90 Drying loss (%) <5 Annealing loss (%) 5.0 to 15 C content (%) 0.5 to 12 pH 4 to 8.

Abstract: Silicon-aluminum mixed oxide powder which is flame-hydrolytically produced and has a composition of 65 to 85% by weight Al.sub.2 O.sub.3, remainder SiO.sub.2 and an amorphous structure, in which each primary particle contains components of SiO.sub.2 and of Al.sub.2 O.sub.3, the primary particles are between 7 and 80 nm, preferably 10 and 40 nm in size and the specific surface of the powder is between 20 and 200 m.sup.2 /g. The powder is used for the production of mullite and sintered compacts manufactured from it.

Abstract: Surface-modified, pyrogenically produced titanium dioxide which is has the following physico-chemical properties:______________________________________ Surface (m.sup.2 /g) 5 to 120 Stamping density (g/l) 50 to 250 Drying loss (%) <5 Annealing loss (%) 3.5 to 15 Carbon content (%) 0.5 to 12 pH 4 to 10.

Abstract: Finely divided precipitated silica with high structure and a______________________________________ BET surface (DIN 66 132) of 150 to 350 m.sup.2 /g Stamping density (DIN 53 194) between 60 and 120 g/l DBP number between 3.0 and 4.0 ml/g Particle size distribution at least 70% from 1 to 6 .mu.m ______________________________________can be prepared by heating a mixture of water and sodium silicate under agitation to a temperature of 70.degree. to 80.degree. C., adding concentrated sulfuric acid into this mixture until half of the alkali present has been neutralized, shearing the reaction mixture and optionally raising the temperature at the same time to 86.+-.5.degree. C. Concentrated sulfuric acid is added after a period of 30 to 120 minutes at a rather high rate until the pH of the silica suspension produced is 3.0 to 3.