Abstract: A method for producing a selective diamond-coated substrate, wherein the diamond-coated substrate includes: a substrate having surfaces including cemented carbide material, areas selected to be coated, and areas not selected to be coated; and one or more diamond coatings on the areas selected to be coated, the method including following steps in order: a first masking step, wherein the areas not selected to be coated but could be chemically attacked during a chemical pre-treatment step, are masked by applying a latex-mask covering these areas; one or more chemical pre-treatment steps; a mask-removing step, wherein the latex-mask is removed; a second masking step, wherein the areas of the substrate surfaces from which the latex-mask was removed and not selected to be coated but could be coated with one or more diamond coatings during one or more coating steps, are covered with one or more masking-covers; and one or more coating steps.

Abstract: The invention refers to a method and apparatus for CVD coating and to a coated body. To improve the mechanical properties of the structure and surface of the body and to make the method and apparatus as simple and cost-effective as possible, it is suggested in the method, in which a layer is deposited on a substrate in a carbon-containing gas atmosphere: that the process parameters be varied during the coating period in such a way that during the coating period a first operating mode and a second operating mode are repeatedly alternated, wherein in the first operating mode a higher carbon over-saturation of the gas atmosphere occurs near the substrate, and in the second operating mode a lower carbon over-saturation of the gas atmosphere occurs near the substrate. In this way, a body can be produced with a substrate and at least one layer deposited on the surface of the substrate, wherein the layer consists of nano-crystalline diamond.

Abstract: The invention refers to a method and apparatus for CVD coating and to a coated body. To improve the mechanical properties of the structure and surface of the body and to make the method and apparatus as simple and cost-effective as possible, it is suggested in the method, in which a layer is deposited on a substrate in a carbon-containing gas atmosphere: that the process parameters be varied during the coating period in such a way that during the coating period a first operating mode and a second operating mode are repeatedly alternated, wherein in the first operating mode a higher carbon over-saturation of the gas atmosphere occurs near the substrate, and in the second operating mode a lower carbon over-saturation of the gas atmosphere occurs near the substrate. In this way, a body can be produced with a substrate and at least one layer deposited on the surface of the substrate, wherein the layer consists of nano-crystalline diamond.

Abstract: Disclosed are an element comprising a hard metal substrate (10) and a diamond layer (30), and a method for coating a hard metal substrate (10). Said hard metal substrate is provided with hard material particles (20) and surrounding binder material (22). The hard material particles (20) are surrounded by binding material (22) in a first area (24) comprising intact hard metal. The transition region of the first area (24) encompasses a deep profile having recesses (18) and elevations (16). The diamond layer (30) is braced with the substrate material (10) with the aid of said deep profile, portions of the diamond layer (30) being disposed deeper within the substrate (10) than elevations (16) of the first area (24). Said structure is obtained by means of a pretreatment process in which a hard metal substrate (10) is first subjected to selective etching in order to remove the binding material (22). A porous zone having a deep profile is formed.