Abstract: The invention relates to a process for making a hot stamped coated steel sheet product, comprising the steps of pre-coating a steel strip or sheet with aluminum- or aluminum alloy, cutting said pre-coated steel strip or sheet to obtain a pre-coated steel blank, heating the blank in a furnace preheated to a temperature and during a time defined by diagram according to thickness, at a heating rate Vc between 20 and 700° C. comprised between 4 and 12° C./s and at a heating rate Vc? between 500 and 700° C. comprised between 1.5 and 6° C./s, to obtain a heated blank; then transferring said heated blank to a die, hot stamping the heated blank in the die obtain a hot stamped steel sheet product, cooling at a mean rate Vr between the exit of the heated blank from the furnace, down to 400° C., of at least 30° C./s.

Abstract: Coated steel having a well defined and uniform thickness is useful and advantageous for preparing products by hot stamping. Products prepared by hot stamping such a steel are particularly advantageous when subjected to a subsequent spot welding step.

Abstract: Coated steel having a well defined and uniform thickness is useful and advantageous for preparing products by hot stamping. Products prepared by hot stamping such a steel are particularly advantageous when subjected to a subsequent spot welding step.

Abstract: The invention relates to a process for making a hot stamped coated steel sheet product, comprising the steps of pre-coating a steel strip or sheet with aluminium- or aluminium alloy, cutting said pre-coated steel strip or sheet to obtain a pre-coated steel blank, heating the blank in a furnace preheated to a temperature and during a time defined by diagram according to thickness, at a heating rate Vc between 20 and 700° C. comprised between 4 and 12° C./s and at a heating rate Vc? between 500 and 700° C. comprised between 1.5 and 6° C./s, to obtain a heated blank; then transferring said heated blank to a die, hot stamping the heated blank in the die obtain a hot stamped steel sheet product, cooling at a mean rate Vr between the exit of the heated blank from the furnace, down to 400° C., of at least 30° C./s.

Abstract: The invention relates to a process for making a hot stamped coated steel sheet product, comprising the steps of pre-coating a steel strip or sheet with aluminium-or aluminium alloy, cutting said pre-coated steel strip or sheet to obtain a pre-coated steel blank, heating the blank in a furnace preheated to a temperature and during a time defined by diagram according to thickness, at a heating rate Vc between 20 and 700° C. comprised between 4 and 12° C./s and at a heating rate Vc? between 500 and 700° C. comprised between 1.5 and 6° C./s, to obtain a heated blank; then transferring said heated blank to a die, hot stamping the heated blank in the die obtain a hot stamped steel sheet product, cooling at a mean rate Vr between the exit of the heated blank from the furnace, down to 400° C., of at least 30° C./s.

Abstract: Coated steel having a well defined and uniform thickness is useful and advantageous for preparing products by hot stamping. Products prepared by hot stamping such a steel are particularly advantageous when subjected to a subsequent spot welding step.

Abstract: The invention relates to a process for making a hot stamped coated steel sheet product, comprising the steps of pre-coating a steel strip or sheet with aluminium—or aluminium alloy, cutting said pre-coated steel strip or sheet to obtain a pre-coated steel blank, heating the blank in a furnace preheated to a temperature and during a time defined by diagram according to thickness, at a heating rate VC between 20 and 700° C. comprised between 4 and 12° C./s and at a heating rate VC? between 500 and 700° C. comprised between 1.5 and 6° C./s, to obtain a heated blank; then transferring said heated blank to a die, hot stamping the heated blank in the die obtain a hot stamped steel sheet product, cooling at a mean rate Vr between the exit of the heated blank from the furnace, down to 400° C., of at least 30° C./s.

Abstract: Hot-rolled steel sheet which then can be cold-rolled, coated, the steel in the sheet having the following composition by weight: 0.15%<carbon<0.5% 0.5%<manganese<3% 0.1%<silicon<0.5% 0.01%<chromium<1% titanium<0.2% aluminum<0.1% phosphorus<0.1% sulfur<0.05% 0.0005%<boron<0.08%, the remainder being iron and impurities inherent in processing, the sheet ensuring a very high mechanical resistance after thermal treatment and the aluminum-based coating ensuring a high resistance to corrosion.

Abstract: The invention relates to an exhaust muffler for a motor vehicle, consisting of an external casing (1), an internal casing (2) and a central part (3) consisting of perforated tubing (4) and transverse partitions (5) assembled together to form a chicane, called the insides. The central part (3) is made of an enameled steel, the steel having the following composition in thousandths of a percent by weight:carbon between 0 and 100manganese between 0 and 500phosphorus between 0 and 30sulfur between 0 and 40aluminum between 0 and 60titanium between 0 and 200copper between 0 and 60nitrogen between 0 and 15,the remainder being iron and residual impurities, said steel being obtained by hot rolling at a final rolling temperature exceeding the Ar.sub.3 point to obtain a strip, which is coiled at a temperature higher than 600 degrees Celsius and, after cold rolling, is subjected to a recrystallization annealing.

Abstract: Hot-rolled steel sheet which then can be cold-rolled, coated, the steel in the sheet having the following composition by weight: 0.15%<carbon<0.5% 0.5%<manganese<3% 0.1%<silicon<0.5% 0.01%<chromium<1% titanium<0.2% aluminum<0.1% phosphorus<0.1% sulfur<0.05% 0.0005%<boron<0.08%, the remainder being iron and impurities inherent in processing, the sheet ensuring a very high mechanical resistance after thermal treatment and the aluminum-based coating ensuring a high resistance to corrosion.