Abstract: The invention relates to a method for manufacturing dielectric ceramic powder and a multilayer ceramic capacitor using the ceramic powder. According to the invention, BaCO3 powder is dispersed into a solution of solvent and dispersant to prepare BaCO3 slurry and then the resultant BaCO3 slurry is wet-milled. Also, TiO2 powder slurry is mixed into the wet-milled BaCO3 slurry to form mixed slurry and then the mixed slurry is dried into mixed powder. Finally, the dried mixed powder is calcined to produce BaTiO3 powder.

Abstract: The invention relates to a method for manufacturing dielectric ceramic powder and a multilayer ceramic capacitor using the ceramic powder. According to the invention, BaCO3 powder is dispersed into a solution of solvent and dispersant to prepare BaCO3 slurry and then the resultant BaCO3 slurry is wet-milled. Also, TiO2 powder slurry is mixed into the wet-milled BaCO3 slurry to form mixed slurry and then the mixed slurry is dried into mixed powder. Finally, the dried mixed powder is calcined to produce BaTiO3 powder.

Abstract: A glass frit for dielectrics, a dielectric ceramic composition, a multilayer ceramic capacitor, and a method for manufacturing the same are disclosed. The glass frit has a composition represented by the formula aSiO2-bB2O3-cLi2O-dK2O-eCaO-fAl2O3-gTiO2-hZrO2, wherein the ratio of components satisfies the conditions of 20?a?35, 20?b?35, 20?c?30, 3?d?5, 2?e?12, 2?f?10, 1?g?12 and 1?h?7 in terms of mol % where a+b+c+d+e+f+g+h=100. The dielectric ceramic composition comprises 100 parts by weight of (Ca1-xRx)(Zr1-yTiy)O3, 0.5˜2.5 parts by weight of the glass frit, and 1.0˜5.0 parts by weight of a Mn compound. Additionally, the multilayer ceramic capacitor, and the method for manufacturing the same also use the glass frit having the above composition. The ratio of tetracoordinate boron to tricoordinate boron is increased in a lithium borosilicate glass, thereby enhancing structural property, and the components of Al2O3, TiO2 and ZrO2, enhance acid resistance.