Abstract: The present invention discloses an aluminosilicate glass composition, aluminosilicate glass and a preparation method therefor and application thereof. Based on the total molar weight of the aluminosilicate glass composition, the aluminosilicate glass composition comprises, by oxide, 67-74 mol % of SiO2, 10-15 mol % of Al2O3, 0-5 mol % of B2O3, 1-10 mol % of MgO, 1-10 mol % of CaO, 0-3 mol % of SrO, 2-8 mol % of BaO, 0.1-4 mol % of ZnO, 0.1-4 mol % of RE2O3 and less than 0.05 mol % of R2O, wherein RE represents rare earth elements, and R represents alkali metals.

Abstract: The invention relates to the field of glass manufacturing, and discloses non-alkali aluminum silicate glass and a preparation method as well as application thereof. A glass melt of the non-alkali aluminum silicate glass at 1600° C. has a resistivity of 200 ?·cm or less; a temperature T35000 corresponding to 35000 P viscosity is 1250° C. or more; an annealing point corresponding to 1013 P viscosity is 790° C. or more, based on a total molar weight of the non-alkali aluminum silicate glass, the non-alkali aluminum silicate glass comprises, by oxide, 69-73 mol % of SiO2, 11-15 mol % of Al2O3, 0-2 mol % of B2O3, 2-8 mol % of MgO, 2-8 mol % of CaO, 0-3 mol % of SrO, 3-10 mol % of BaO, 0.1-2 mol % of ZnO, 0.02-0.7 mol % of RE2O3, 0.01-0.5 mol % of Se2O3 and R2O, less than 0.05 mol %, wherein RE represents rare earth elements, and R represents alkali metals.

Abstract: A composition for glass, and aluminosilicate glass, preparation method therefor, and use thereof. In molar percentage, in the composition, the total content of SiO2, B2O3, P2O5, GeO2 and TeO2 is 60˜85 mol %; the total content of Al2O3 and Ga2O3 is 3˜20 mol %; the total content of ZnO and Y2O3 is 0.1˜5 mol %; and the total content of alkaline earth metal oxide is 4˜30 mol %. The glass has a high strain point, a low melting temperature, and a high thermal expansion coefficient, has good toughness, and is suitable for large-scale industrial production.

Abstract: The present disclosure relates to glass manufacturing, a glass composition, glass with a low inclusion content and a preparation method therefor and use thereof. The composition comprises 50-64 wt. % SiO2, 14-24 wt. % Al2O3, 0-7 wt. % B2O3+P2O5, 0.5-7 wt. % MgO, 1-10 wt. % CaO, 0-9 wt. % SrO, 0.1-14 wt. % BaO, 0.1-5 wt. % ZnO, 0.1-4 wt. % TiO2, 0.1-7 wt. % Y2O3+La2O3+Nd2O3, and <0.05 wt. % R2O, wherein R2O is a sum of the content of Li2O, Na2O and K2O, and the composition satisfies the following conditions: (1) a temperature T100 corresponding to a viscosity of 100 P is 1730° C. or higher; (2) a surface tension at 1300° C. is less than 420 mN/m. The glass prepared by the glass composition and the glass with a low inclusion content preparation method has the advantages of having low inclusion content, having a simple preparation process, being low in cost and so on.

Abstract: The invention provides a composition for glass, a glass, and a preparation method and application thereof. On an oxide basis, the composition for glass contains 45-64 wt % SiO2, 16-26 wt % Al2O3, 0.1-2 wt % MgO, 10-17 wt % Na2O, 0.5-15 wt % P2O5, and optionally 0-2 wt % TiO2. The glass prepared from the composition for glass has a higher chemical resistance, a higher strain point, and a higher compressive stress and depth of compressive stress layer formed on the glass surface, and the glass has a higher Young's modulus.

Abstract: A composition for glass, alkaline earth aluminosilicate glass, and a preparation method therefor and applications thereof. Based on the total number of moles of each component and the counting of oxides, the composition contains 68-73 mol % of SiO2, 11.5-15 mol % of Al2O3, 2-6 mol % of MgO, 2.5-7.5 mol % of CaO, 0-3 mol % of SrO, 2-7 mol % of BaO, 0-4 mol % of ZnO and 0.05-1.5 mol % of TiO2. The glass has a high strain point, a high Young's modulus, a high specific modulus, a high Vickers hardness, high chemical stability, a high refractive index and high glass formation stability, and has a lower forming temperature, a lower melting temperature, a lower thermal expansion coefficient, a lower surface tension, a lower density, and low glass manufacturing difficulty.

Abstract: The present invention relates to the field of glass manufacturing, and discloses aluminoborosilicate glass, and a preparation method and an application thereof. Based on the total weight of components in the composition of the glass, the glass comprises: 33-60 wt % SiO2, 3-10 wt % Al2O3, 10-30 wt % B2O3, 1-15 wt % ZnO+TiO2+Sc2O3, and 7-27 wt % alkaline-earth oxide RO, wherein RO is at least one of MgO, CaO, SrO and BaO, and 0.001 wt %?Sc2O3?1 wt%. The aluminoborosilicate glass provided in the present invention has advantages including low density, high index of refraction, low thermal expansion coefficient, high thermostability, high flexibility, and easy bending, etc.

Abstract: The invention discloses a composition for preparing glass, a glass article and a use thereof, and a glass article made from the composition. The glass article is preferably a glass substrate made from a composition with an M value of from about 1 to about 10 as calculated by the empirical equation: M=0.13×wt (B2O3)×wt (B2O3)+0.42×wt (CaO)+0.55×wt (MgO)+0.75×wt (SrO)?0.05×wt (Al2O3)×wt (Al2O3). A use of the glass article (especially the glass substrate) for manufacturing a display device is disclosed herein, wherein the glass article has better properties, such as lowered content of solid inclusions and gas inclusions, lowered thickness range and lowered warpage.

Abstract: The invention relates to the field of glass manufacturing, and discloses non-alkali aluminum silicate glass and a preparation method as well as application thereof. A glass melt of the non-alkali aluminum silicate glass at 1600° C. has a resistivity of 200 ?·cm or less; a temperature T35000 corresponding to 35000 P viscosity is 1250° C. or more; an annealing point corresponding to 1013 P viscosity is 790° C. or more, based on a total molar weight of the non-alkali aluminum silicate glass, the non-alkali aluminum silicate glass comprises, by oxide, 69-73 mol % of SiO2, 11-15 mol % of Al2O3, 0-2 mol % of B2O3, 2-8 mol % of MgO, 2-8 mol % of CaO, 0-3 mol % of SrO, 3-10 mol % of BaO, 0.1-2 mol % of ZnO, 0.02-0.7 mol % of RE2O3, 0.01-0.5 mol % of Se2O3 and R2O, less than 0.05 mol %, wherein RE represents rare earth elements, and R represents alkali metals.

Abstract: The present invention discloses an aluminosilicate glass composition, aluminosilicate glass and a preparation method therefor and application thereof. Based on the total molar weight of the aluminosilicate glass composition, the aluminosilicate glass composition comprises, by oxide, 67-74 mol % of SiO2, 10-15 mol % of Al2O3, 0-5 mol % of B2O3, 1-10 mol % of MgO, 1-10 mol % of CaO, 0-3 mol % of SrO, 2-8 mol % of BaO, 0.1-4 mol % of ZnO, 0.1-4 mol % of RE2O3 and less than 0.05 mol % of R2O, wherein RE represents rare earth elements, and R represents alkali metals.

Abstract: The invention provides a composition for glass, a glass, and a preparation method and application thereof. On an oxide basis, the composition for glass contains 45-64 wt % SiO2, 16-26 wt % Al2O3, 0.1-2 wt % MgO, 10-17 wt % Na2O, 0.5-15 wt % P2O5, and optionally 0-2 wt % TiO2. The glass prepared from the composition for glass has a higher chemical resistance, a higher strain point, and a higher compressive stress and depth of compressive stress layer formed on the glass surface, and the glass has a higher Young's modulus.

Abstract: A composition for glass, alkaline earth aluminosilicate glass, and a preparation method therefor and applications thereof. Based on the total number of moles of each component and the counting of oxides, the composition contains 68-73 mol % of SiO2, 11.5-15 mol % of Al2O3, 2-6 mol % of MgO, 2.5-7.5 mol % of CaO, 0-3 mol % of SrO, 2-7 mol % of BaO, 0-4 mol % of ZnO and 0.05-1.5 mol % of TiO2. The glass has a high strain point, a high Young's modulus, a high specific modulus, a high Vickers hardness, high chemical stability, a high refractive index and high glass formation stability, and has a lower forming temperature, a lower melting temperature, a lower thermal expansion coefficient, a lower surface tension, a lower density, and low glass manufacturing difficulty.

Abstract: The present disclosure relates to glass manufacturing, a glass composition, glass with a low inclusion content and a preparation method therefor and use thereof. The composition comprises 50-64 wt. % SiO2, 14-24 wt. % Al2O3, 0-7 wt. % B2O3+P2O5, 0.5-7 wt. % MgO, 1-10 wt. % CaO, 0-9 wt. % SrO, 0.1-14 wt. % BaO, 0.1-5 wt. % ZnO, 0.1-4 wt. % TiO2, 0.1-7 wt. % Y2O3+La2O3+Nd2O3, and <0.05 wt. % R2O, wherein R2O is a sum of the content of Li2O, Na2O and K2O, and the composition satisfies the following conditions: (1) a temperature T100 corresponding to a viscosity of 100 P is 1730° C. or higher; (2) a surface tension at 1300° C. is less than 420 mN/m. The glass prepared by the glass composition and the glass with a low inclusion content preparation method has the advantages of having low inclusion content, having a simple preparation process, being low in cost and so on.

Abstract: A composition for glass, and aluminosilicate glass, preparation method therefor, and use thereof. In molar percentage, in the composition, the total content of SiO2, B2O3, P2O5, GeO2 and TeO2 is 60˜85 mol %; the total content of Al2O3 and Ga2O3 is 3˜20 mol %; the total content of ZnO and Y2O3 is 0.1˜5 mol %; and the total content of alkaline earth metal oxide is 4˜30 mol %. The glass has a high strain point, a low melting temperature, and a high thermal expansion coefficient, has good toughness, and is suitable for large-scale industrial production.

Abstract: The present invention relates to the field of glass manufacturing, and discloses aluminoborosilicate glass, and a preparation method and an application thereof. Based on the total weight of components in the composition of the glass, the glass comprises: 33-60 wt % SiO2, 3-10 wt % Al2O3, 10-30 wt % B2O3, 1-15 wt % ZnO+TiO2+Sc2O3, and 7-27 wt % alkali-earth oxide RO, wherein RO is at least one of MgO, CaO, SrO and BaO, and 0.001 wt %?Sc2O3?1 wt %. The aluminoborosilicate glass provided in the present invention has advantages including low density, high index of refraction, low thermal expansion coefficient, high thermostability, high flexibility, and easy bending, etc.

Abstract: The invention discloses a composition for preparing glass, a glass article and a use thereof, and a glass article made from the composition. The glass article is preferably a glass substrate made from a composition with an M value of from about 1 to about 10 as calculated by the empirical equation: M=0.13×wt (B2O3)×wt (B2O3)+0.42×wt (CaO)+0.55×wt (MgO)+0.75×wt (SrO)?0.05×wt (Al2O3)×wt (Al2O3). A use of the glass article (especially the glass substrate) for manufacturing a display device is disclosed herein, wherein the glass article has better properties, such as lowered content of solid inclusions and gas inclusions, lowered thickness range and lowered warpage.