Abstract: A method for producing a high strength steel sheet having a yield strength YS>850 MPa, a tensile strength TS>1180 MPa, a total elongation >13% and a hole expansion ratio HER>30%, by heat treating a steel sheet wherein the chemical composition of the steel contains: 0.13%?C?0.22%, 1.2%?Si?1.8%, 1.8%?Mn?2.2%, 0.10%?Mo?0.20%, Nb?0.05%, Ti<0.05%, Al?0.5%, the remainder being Fe and unavoidable impurities. The sheet is annealed at an annealing temperature TA>865° C. and <1000° C. for a time of more than 30 s, then quenched by cooling it to a quenching temperature QT between 275° C. and 375° C., at a cooling speed >30° C./s in order to have, just after quenching, a structure consisting of austenite and at least 50% of martensite, the austenite content being such that the final structure can contain between 3% and 15% of residual austenite and between 85% and 97% of the sum of martensite and bainite without ferrite, then heated to a partitioning temperature PT between 370° C. and 470° C.

Abstract: The invention deals with a cold rolled and hot dip steel sheet, with a tensile strength of at least 980 MPa, with yield strength above or equal to 500 MPa, with total elongation above or equal to 8%, the composition consisting by weight percent: 0.05<C<0.15%, 2<Mn?3%, Al<0.1%, 0.3<Si<1.5%, 0.01%<Nb<0.05%, N<0.02%, 0.1<Cr+Mo<1%, 0.0001<B<0.0025, Ti<0.5%, V<0.01%, S<0.01%, P<0.05% the remainder of the composition being iron and unavoidable impurities resulting from the smelting and the microstructure contains, in surface fraction: between 50 and 95% of martensite and between 5 and 50% of the sum of ferrite and bainite, wherein the ferrite grain size is below 10????, and wherein the aspect ratio of the ferrite grain size is between 1 and 3. The steel according to the invention is oxidized and subsequently reduced during heating, soaking and cooling steps of the annealing.

Abstract: A method for producing a high strength steel sheet having a yield strength YS of at least 850 MPa, a tensile strength TS of at least 1180 MPa, a total elongation of at least 14% and a hole expansion ratio HER of at least 30%. The chemical composition of the steel contains: 0.15%?C?0.25%, 1.2%?Si?1.8%, 2%?Mn?2.4%, 0.1%?Cr?0.25%, Nb?0.05%, Ti?0.05%, Al?0.50%, the remainder being Fe and unavoidable impurities. The sheet is annealed at an annealing temperature TA higher than Ac3 but less than 1000° C. for more than 30 s, by cooling it to a quenching temperature QT between 275° C. and 325° C., at a cooling speed sufficient to have, just after quenching, a structure consisting of austenite and at least 50% of martensite, the austenite content en.) being such that the final structure can contain between 3% and 15% of residual austenite and between 85 and 97% of the sum of martensite and bainite, without ferrite, heated to a partitioning temperature PT between 420° C. and 470° C.