Abstract: Crystalline zirconium oxide powder with a BET surface of less than 30 m.sup.2 /g, preferably 10 to 20 m.sup.2 /g, a primary particle size of 0.1 to 0.5 .mu.m, a monoclinic crystal structure and, optionally, a content of Y.sub.2 O.sub.3 of 1 to 10% by weight and/or of 1 to 10% by wt. MgO.It is produced by adding an aqueous zirconium salt solution optionally containing yttrium ions and/or magnesium ions under agitation into a vessel which contains an aqueous base solution such as e.g. sodium hydroxide solution with a content of NaOH which corresponds to an excess of at least 0.5 mole/l NaOH. The mixture obtained in this manner is then treated hydrothermally at a temperature of 200.degree. to 400.degree. C., the product obtained is separated by filtration, washed chloride-free with water and dried at 100.degree. to 120.degree. C.The zirconium oxide powder can be used to produce sintered ceramics.

Abstract: Crystalline zirconium oxide powder with a BET surface of less than 30 m.sup.2 /g, preferably 10 to 20 m.sup.2 /g, a primary particle size of 0.1 to 0.5 .mu.m, a monoclinic crystal structure and, optionally, a content of Y.sub.2 O.sub.3 of 1 to 10% by weight and/or of 1 to 10% by wt. MgO.It is produced by adding an aqueous zirconium salt solution optionally containing yttrium ions and/or magnesium ions under agitation into a vessel which contains an aqueous base solution such as e.g. sodium hydroxide solution with a content of NaOH which corresponds to an excess of at least 0.5 mole/l NaOH. The mixture obtained in this manner is then treated hydrothermally at a temperature of 200.degree. to 400.degree. C., the product obtained is separated by filtration, washed chloride-free with water and dried at 100.degree. to 120.degree. C.The zirconium oxide powder can be used to produce sintered ceramics.

Abstract: Crystalline zirconium oxide powder with a BET surface of less than 30 m.sup.2 /g, preferably 10 to 20 m.sup.2 /g, a primary particle size of 0.1 to 0.5 .mu.m, a monoclinic crystal structure and, optionally, a content of Y.sub.2 O.sub.3 of 1 to 10% by weight and/or of 1 to 10 % by wt. MgO.It is produced by adding an aqueous zirconium salt solution optionally containing yttrium ions and/or magnesium ions under agitation into a vessel which contains an aqueous base solution such as e.g. sodium hydroxide solution with a content of NaOH which corresponds to an excess of at least 0.5 mole/1 NaOH. The mixture obtained in this manner is then treated hydrothermally at a temperature of 200.degree. to 400.degree. C., the product obtained is separated by filtration, washed chloride-free with water and dried at 100.degree. to 200.degree. C.The zirconium oxide power can be used to produce sintered ceramics.