Abstract: A method of forming high strength glass fibers in a refractory-lined glass melter, products made there from and batch compositions suited for use in the method are disclosed. The glass composition for use in the method of the present invention is up to about 64-75 weight percent SiO2, 16-24 weight percent Al2O3, 8-12 weight percent MgO and 0.25-3 weight percent R2O, where R2O equals the sum of Li2O and Na2O, has a fiberizing temperature less than about 2650° F., and a ?T of at least 80° F. By using oxide-based refractory-lined furnaces the cost of production of glass fibers is substantially reduced in comparison with the cost of fibers produced using a platinum-lined melting furnace. High strength composite articles including the high strength glass fibers are also disclosed.

Abstract: A method of forming high strength glass fibers in a refractory-lined glass melter, products made there from and batch compositions suited for use in the method are disclosed. The glass composition for use in the method of the present invention is up to about 64-75 weight percent SiO2, 16-24 weight percent Al2O3, 8-12 weight percent MgO and 0.25-3 weight percent R2O, where R2O equals the sum of Li2O and Na2O, has a fiberizing temperature less than about 2650° F., and a ?T of at least 80° F. By using oxide-based refractory-lined furnaces the cost of production of glass fibers is substantially reduced in comparison with the cost of fibers produced using a platinum-lined melting furnace. High strength composite articles including the high strength glass fibers are also disclosed.

Abstract: A method of forming high strength glass fibers in a refractory lined glass melter is disclosed. The refractory lined melter is suited to the batch compositions disclosed for the formation high modulus, and high-strength glass fibers. The glass composition for use in the method of the present invention is up to about 70.5 Weight % SiO2, 24.5 weight % Al2O3, 22 weight % alkaline earth oxides and may include small amounts of alkali metal oxides and ZrO2. Oxide based refractories included alumina, chromic oxide, silica, alumina-silica, zircon, zirconia-alumina-silica and combinations thereof. By using oxide based refractory lined furnaces the cost of production of glass fibers is substantially reduced in comparison with the cost of fibers using a platinum lined melting furnace. Fibers formed by the present invention are also disclosed.

Abstract: A method of forming high strength glass fibers in a refractory lined glass melter is disclosed. The refractory lined melter is suited to the batch compositions disclosed for the formation high modulus, and high-strength glass fibers. The glass composition for use in the method of the present invention is up to about 70.5 Weight % SiO2, 24.5 weight % Al2O3, 22 weight % alkaline earth oxides and may include small amounts of alkali metal oxides and ZrO2. Oxide based refractories included alumina, chromic oxide, silica, alumina-silica, zircon, zirconia-alumina-silica and combinations thereof. By using oxide based refractory lined furnaces the cost of production of glass fibers is substantially reduced in comparison with the cost of fibers using a platinum lined melting furnace. Fibers formed by the present invention are also disclosed.

Abstract: Stabilized substantially fluid-impervious microencapsulated delivery vehicles comprising an active agent are disclosed. The microencapsulated delivery vehicles have improved rupture force strength. In one embodiment, the microencapsulated delivery vehicles are heat delivery vehicles capable of generating heat upon activation. The microencapsulated heat delivery vehicles may be introduced into wet wipes such that, upon activation, the wet wipe solution is warmed resulting in a warm sensation on a user's skin. Any number of other active ingredients, such as cooling agents and biocides, can also be incorporated into a microencapsulated delivery vehicle.

Abstract: A method of forming high strength glass fibers in a refractory lined glass melter is disclosed. The refractory fined melter is suited to the batch compositions disclosed for the formation high modulus, and high-strength glass fibers. The glass composition for use in the method of the present invention is up to about 70.5 Weight % SiO2, 24.5 weight % Al2O3, 22 weight % alkaline earth oxides and may include small amounts of alkali metal oxides and ZrO2. Oxide based refractories included alumina, chromic oxide, silica, alumina-silica, zircon, zirconia-alumina-silica and combinations thereof. By using oxide based refractory lined furnaces the cost of production of glass fibers is substantially reduced in comparison with the cost of fibers using a platinum lined melting furnace. Fibers formed by the present invention are also disclosed.