Abstract: Despite the frangibility of additive-free granules of brominated anionic styrenic polymer, it has been found possible by use of special mechanical processing to provide pellets of unadulterated brominated anionic styrenic polymer having a bromine content of at least about 50 wt % and in which at least about 70 wt % (preferably at least about 75 wt %) of the pellets are retained on a standard US No. 40 sieve and no more than about 30 wt % (preferably no more than about 25 wt %) are retained on a standard US No. 5 sieve. In preferred embodiments such pelletized anionic styrenic polymer is brominated anionic polystyrene having a bromine content of at least about 67 wt %, e.g., in the range of about 67 to about 71 wt %. Also preferred are pelletized brominated anionic styrenic polymers in which the melt flow index (ASTM D 1238-99) at 220° C., 2.16 kg is at least 4 g/10 min and preferably is at least 5 g/10 min.

Abstract: Disclosed are flame retardant compositions comprised of (a) brominated anionic styrenic polymer, and (b) at least one polybrominated alpha-omega diphenylalkane having a total of at least 6 bromine atoms directly bonded to the phenyl rings and in the range of 1 to 6 carbon atoms in the alkylene group disposed between the phenyl groups, and specified flame retarded polymer compositions with which have been blended (a) and (b) individually or in combination.

Abstract: This invention provides a multimodal brominated anionic styrenic polymer composition. The composition is comprised of at least two brominated anionic styrenic polymer weight fractions which have different weight average molecular weights. Also provided by this invention are processes for producing multimodal brominated anionic styrenic polymer compositions.

Abstract: This invention provides a multimodal brominated styrenic polymer composition. The composition is comprised of at least one brominated anionic styrenic polymer and at least one brominated non-anionic styrenic polymer. Also provided by this invention are processes for producing multimodal brominated styrenic polymer compositions.

Abstract: A fiber or filament which is formed from ingredients comprising (a) at least one fiber-forming thermoplastic polymer and (b) at least one polybrominated anionic styrenic polymer is provided. The polybrominated anionic styrenic polymer has a bromine content of at least about 50 wt %, and a GPC weight average molecular weight in the range of about 5000 to about 40,000, or a GPC weight average molecular weight of at least about 600,000. When the fiber-forming thermoplastic polymer is a polyester, the polybrominated anionic styrenic polymer is present in a flame resistant or flame retardant amount. When the fiber-forming thermoplastic polymer is a polyamide, the polybrominated anionic styrenic polymer is at least about 2 wt % of the fiber or filament. When the fiber-forming thermoplastic polymer is a polyolefin, at least one synergist is present and the polybrominated anionic styrenic polymer is no more than about 15 wt % of the fiber or filament.

Abstract: Disclosed are flame retardant compositions comprised of (a) brominated anionic styrenic polymer, and (b) at least one polybrominated alpha-omega diphenylalkane having a total of at least 6 bromine atoms directly bonded to the phenyl rings and in the range of 1 to 6 carbon atoms in the alkylene group disposed between the phenyl groups, and specified flame retarded polymer compositions with which have been blended (a) and (b) individually or in combination.