Abstract: A process for forming a coated substrate comprises providing a nickel base alloy substrate, depositing a chromium coating onto the nickel base alloy substrate and diffusing chromium from said coating into the substrate, applying a MCrAlY coating onto the nickel base alloy substrate and heat treating the substrate with the deposited chromium and the MCrAlY coating so that chromium diffuses into an outer region of the substrate. Further, in accordance with the present invention, a strip process for removing a coating from a substrate broadly comprises the steps of providing a nickel base alloy substrate having chromium diffused into an outer region and a MCrAlY coating deposited over the substrate with the diffused chromium and removing the MCrAlY coating by immersing the nickel base alloy substrate in an acid solution containing a sulfuric acid-hydrochloric acid mixture in water.

Abstract: A process for forming a coated substrate comprises providing a nickel base alloy substrate, depositing a chromium coating onto the nickel base alloy substrate and diffusing chromium from said coating into the substrate, applying a MCrAlY coating onto the nickel base alloy substrate and heat treating the substrate with the deposited chromium and the MCrAlY coating so that chromium diffuses into an outer region of the substrate. Further, in accordance with the present invention, a strip process for removing a coating from a substrate broadly comprises the steps of providing a nickel base alloy substrate having chromium diffused into an outer region and a MCrAlY coating deposited over the substrate with the diffused chromium and removing the MCrAlY coating by immersing the nickel base alloy substrate in an acid solution containing a sulfuric acid—hydrochloric acid mixture in water.

Abstract: A process for reducing secondary reaction zone formation articles includes the steps of non-selective removing an external surface of an as-cast article free of coating to form an as-cast article having a surface substantially free of residual surface stress; and applying a coating material upon the surface substantially free of residual surface stress to form a coated as-cast article having a coating layer disposed upon the surface substantially free of residual surface stress.

Abstract: A shot peening operation is developed utilizing a test strip and test strip holder. The test strip holder has an internal cavity, and the test strip lies over that cavity. Parameters of a shot peening operation can be developed utilizing the test strip, and those parameters will be acceptable for use with a part having internal cavities.

Abstract: A process for forming a coated substrate comprises providing a nickel base alloy substrate, depositing a chromium coating onto the nickel base alloy substrate and diffusing chromium from said coating into the substrate, applying a MCrAlY coating onto the nickel base alloy substrate and heat treating the substrate with the deposited chromium and the MCrAlY coating so that chromium diffuses into an outer region of the substrate. Further, in accordance with the present invention, a strip process for removing a coating from a substrate broadly comprises the steps of providing a nickel base alloy substrate having chromium diffused into an outer region and a MCrAlY coating deposited over the substrate with the diffused chromium and removing the MCrAlY coating by immersing the nickel base alloy substrate in an acid solution containing a sulfuric acid-hydrochloric acid mixture in water.

Abstract: Method for forming on a superalloy or other metallic substrate a platinum graded, outward single phase diffusion aluminide coating on a surface of the substrate by depositing a layer comprising Pt on the substrate and then gas phase aluminizing the substrate in a coating chamber having a solid source of aluminum (e.g. aluminum alloy particulates) disposed therein close enough to the surface of the substrate to form at an elevated substrate coating temperature a diffusion aluminide coating having an inner diffusion zone and outer additive single (Ni,Pt)Al phase layer having a concentration of platinum that is relatively higher at an outermost coating region than at an innermost coating region adjacent the diffusion zone.