Abstract: The invention relates to a method for producing supersulfated cement, wherein pozzolanic and hydraulic aluminosilicate components and a calcium-sulfate-alkaline activation complex are mixed together. The calcium-sulfate-alkaline activation complex is produced by carrying out the following successive steps: a first step of mixing 70% by weight of calcium sulfate and 30% by weight of alkaline components; and subsequently; a second step of thermodynamically activating, by hot quenching, the calcium-sulfate-alkaline activation complex; and subsequently; a third step of cold quenching, by rapid mixing, the activated calcium-sulfate-alkaline activation complex with the pozzolanic aluminosilicate components.

Abstract: The invention concerns a granular composition designed to be reacted with water to form a refractory material, characterized in that it comprises an anhydrite III hydraulic binder and an alumina-based granular material. The invention aims at making a cold-processed refractory material which does not necessarily have to be cured prior to use, said material having very good refractory and mechanical properties for high (>1000° C.) and very high (>1600° C.) temperatures.

Abstract: The invention relates to a method for stabilising a metastable soluble anhydrite III, to a method for producing a hydraulic binder based thereon, to the thus obtainable hydraulic binder, to a method for the use thereof in the cement industry and to an industrial plant for carrying out the inventive method. The method consists in stabilising a metastable soluble anhydrite III by mechanically stressing the particles thereof in such a way the crystal structure of the particles is modified and the metastable phase thereof is stabilised. Said invention makes it possible to stabilise the metastable soluble anhydrite III particles without using current steps for heating and quenching said particles.