Abstract: Fatty acid amide coated pigments are obtained and used to formulate with uncolored thermoplastic materials. The colors of the pigments are fully developed, and extremely high pigment loadings are obtained. The coated pigments are formed by admixing the pigment with melted fatty acid amide; solidifying the material by cooling it; grinding the material; and separating out the fines. The coated pigment's particles are compounded with thermoplastic materials by low shear means, such as, injection molding. An improved form of the coated pigments can be obtained by admixing the melted fatty acid amide, and the pigment; extruding the admixture to form a creamy mass; solidifying and forming the creamy mass by passing it through cold and forming rollers; grinding the resultant wafer-like material; and separating out the fines.

Abstract: A method of preparing coated pigment particles for dry compounding with a polymeric material such as plastic or rubber, which method comprises the steps of providing particles of a hydrophilic color pigment, mixing the pigment particles with a wax having a given melting point temperature and a brittle condition below a given lower temperature, heating the mixture above a process temperature substantially above the melting temperature and substantially above the boiling point of water to boil away entrapped water, subjecting the mixture to high shear mixing while at the process temperature, cooling the mixture to a temperature below the given lower temperature to produce a solid mass, and, then, breaking the solid mass into flakes.

Abstract: Fatty acid amide coated pigments are obtained and used to formulate with uncolored thermoplastic materials. The colors of the pigments are fully developed and extremely high pigment loadings are obtained. The coated pigments are formed by admixing the pigment with melted fatty acid amide; solidifying the material by cooling it; grinding the material; and separating out the fines. The coated pigments particles are compounded with thermoplastic materials by low shear means, such as, injection molding. An improved form of the coated pigments can be obtained by admixing the melted fatty acid amide, and the pigment; extruding the admixture to form a creamy mass; solidifying and forming the creamy mass by passing it through cold and forming rollers; grinding the resultant wafer-like material; and separating out the fines.

Abstract: Fatty acid amide coated pigments are obtained and used to formulate with thermoplastic or thermoset materials. The colors of the pigments are fully developed and extremely high pigment loadings are obtained. The coated pigments are formed by admixing the pigment with melted fatty acid amide; solidifying the material by cooling it; grinding the material; and separating out the fines. The coated pigment particles are compounded with thermoplastic or thermoset materials by low shear means, such as, injection molding. An improved form of the coated pigments can be obtained by admixing the melted fatty acid amide and the pigment; extruding the admixture to form a creamy mass; solidifying and forming the creamy mass by passing it through cold and forming rollers; grinding the resultant wafer-like material; and separating out the fines.