Abstract: The present invention provides a metal pipe coated on at least a section of the metal pipe with a polyolefin coating system, wherein the system consists of the following layers: (a) optionally, a corrosion protective layer of a chromate, phosphate or other salt; (b) a polyolefin based adhesive, preferably in a thickness of 0.3-5 mm; (c) a PE or PP coating layer, preferably in a thickness of 1-10 mm; (d) optionally, an adhesion promoting layer between the polyolefin based adhesive and a PE or PP layer; wherein the polyolefin based adhesive contains an organic phase consisting of substantially saturated hydrocarbons, and wherein the adhesive contains amorphous polypropylene, ethylene-propylene copolymers or poly(iso)butylene (co)polymers, said adhesive being flowable when a pressure of 10 kgf/cm2 is applied, wherein the PE or PP coating is a continuous layer over the coated section, and wherein said polyolefin based adhesive adheres to both the metal pipe and to said PE or PP coating.

Abstract: The present invention provides a metal pipe coated on at least a section of the metal pipe with a polyolefin coating system, wherein the system consists of the following layers: (a) optionally, a corrosion protective layer of a chromate, phosphate or other salt; (b) a polyolefin based adhesive, preferably in a thickness of 0.3-5 mm; (c) a PE or PP coating layer, preferably in a thickness of 1-10 mm; (d) optionally, an adhesion promoting layer between the polyolefin based adhesive and a PE or PP layer; wherein the polyolefin based adhesive contains an organic phase consisting of substantially saturated hydrocarbons, and wherein the adhesive contains amorphous polypropylene, ethylene-propylene copolymers or poly(iso)butylene (co)polymers, said adhesive being flowable when a pressure of 10 kgf/cm2 is applied, wherein the PE or PP coating is a continuous layer over the coated section, and wherein said polyolefin based adhesive adheres to both the metal pipe and to said PE or PP coating.

Abstract: The present invention provides a metal pipe coated on at least a section of the metal pipe with a polyolefin coating system, wherein the system consists of the following layers: (a) optionally, a corrosion protective layer of a chromate, phosphate or other salt; (b) a polyolefin based adhesive, preferably in a thickness of 0.3-5 mm; (c) a PE or PP coating layer, preferably in a thickness of 1-10 mm; (d) optionally, an adhesion promoting layer between the polyolefin based adhesive and a PE or PP layer; wherein the polyolefin based adhesive contains an organic phase consisting of substantially saturated hydrocarbons, and wherein the adhesive contains amorphous polypropylene, ethylene-propylene copolymers or poly(iso)butylene (co)polymers, said adhesive being flowable when a pressure of 10 kgf/cm2 is applied, wherein the PE or PP coating is a continuous layer over the coated section, and wherein said polyolefin based adhesive adheres to both the metal pipe and to said PE or PP coating.

Abstract: An adhesive compound consisting essentially of an organic phase and inorganic phase, the organic phase comprising an amorphous aliphatic (co)polymer having a Ring & Ball softening point of between 75 and 180° C., and a second aliphatic material having a Tg of about ?5° C. or lower and a kinematic viscosity of 4500 mm2/s at 100° C. or less, wherein said organic components are present in weight amounts of between 95/5 and 10/90; the inorganic phase comprising a filler, the filler being present in amount of at least about 15 wt % in the total composition. The compositions are suitable for anti-corrosion coatings or sealants against filtration or penetration of water or moisture. A rubber material may be added to this compound or other anti-corrosion coatings to increase the yield point at high temperatures.

Abstract: An adhesive compound consisting essentially of an organic phase and inorganic phase, the organic phase comprising an amorphous aliphatic (co)polymer having a Ring & Ball softening point of between 75 and 180° C., and a second aliphatic material having a Tg of about ?5° C. or lower and a kinematic viscosity of 4500 mm2/s at 100° C. or less, wherein said organic components are present in weight amounts of between 95/5 and 10/90; the inorganic phase comprising a filler, the filler being present in amount of at least about 15 wt % in the total composition. The compositions are suitable for anti-corrosion coatings or sealants against filtration or penetration of water or moisture. A rubber material may be added to this compound or other anti-corrosion coatings to increase the yield point at high temperatures.

Abstract: The present invention relates to an adhesive compound consisting essentially of an organic phase and inorganic phase, the organic phase comprising an amorphous aliphatic (co)polymer having a Ring & Ball softening point of between 75 and 180° C., and a second aliphatic material having a Tg of about ?5° C. or lower and a kinematic viscosity of 4500 mm2/s at 100° C. or less, wherein said organic components are present in weight amounts of between 95/5 and 10/90; the inorganic phase comprising a filler, the filler being present in amount of at least about 15 wt % in the total composition. The compositions are suitable for anti-corrosion coatings or sealants against filtration or penetration of water or moisture. A rubber material may be added to this compound or other anti-corrosion coatings to increase the yield point at high temperatures.

Abstract: The present invention relates to an adhesive compound consisting essentially of an organic phase and inorganic phase, the organic phase comprising an amorphous aliphatic (co)polymer having a Ring & Ball softening point of between 75 and 180° C., and a second aliphatic material having a Tg of about ?5° C. or lower and a kinematic viscosity of 4500 mm2/s at 100° C. or less, wherein said organic components are present in weight amounts of between 95/5 and 10/90; the inorganic phase comprising a filler, the filler being present in amount of at least about 15 wt % in the total composition. The compositions are suitable for anti-corrosion coatings or sealants against filtration or penetration of water or moisture. A rubber material may be added to this compound or other anti-corrosion coatings to increase the yield point at high temperatures.