Abstract: To provide a propylene resin composition excellent in both the electroconductivity and moldability and excellent in their balance, and a molded product thereof. A propylene resin composition comprising from 50 to 98 wt % of a propylene resin having a MFR of from 5 to 300 g/10 min, and from 2 to 50 wt % of carbon black having a 24M4DBP absorption of at least 130 cm3/100 g, a dehydrogenation amount of at most 1.2 mg/g at 1,500° C. for 30 minutes and a crystallite size (Lc) of from 10 to 17 ?. A propylene resin molded product which is a propylene resin molded product obtained by molding such a propylene resin composition and which has a volume resistivity of from 102 to 109 ?·cm and a MFR of from 1 to 80 g/10 min.

Abstract: To provide carbon black which improves the electrical conductivity and flowability of a resin composition. Carbon black characterized by having the following characteristics: 24M4DBP absorption: At least 130 cm3/100 g (1,500° C.×30 min) dehydrogenation amount: At most 1.2 mg/g Crystallite size Lc: From 10 to 17 ? More preferably, it has the following characteristics: Nitrogen adsorption specific surface area: from 150 to 300 m2/g Average particle diameter: from 14 to 24 nm CTAB adsorption specific surface area: from 120 to 220 m2/g DBP absorption: from 150 to 400 cm3/100 g Oxygen-containing functional group density: at most 3 ?mol/m2.

Abstract: To provide a propylene resin composition excellent in both the electroconductivity and moldability and excellent in their balance, and a molded product thereof. A propylene resin composition comprising from 50 to 98 wt % of a propylene resin having a MFR of from 5 to 300 g/10 min, and from 2 to 50 wt % of carbon black having a 24M4DBP absorption of at least 130 cm3/100 g, a dehydrogenation amount of at most 1.2 mg/g at 1,500° C. for 30 minutes and a crystallite size (Lc) of from 10 to 17 ?. A propylene resin molded product which is a propylene resin molded product obtained by molding such a propylene resin composition and which has a volume resistivity of from 102 to 109 ?·cm and a MFR of from 1 to 80 g/10 min.

Abstract: To provide carbon black which improves the electrical conductivity and flowability of a resin composition. Carbon black characterized by having the following characteristics: 24M4DBP absorption: At least 130 cm3/100 g (1,500° C. ×30 min) dehydrogenation amount: At most 1.