Abstract: A resin composition has high flame retardancy and excellent heat resistance, peel strength with copper foil, thermal expansion coefficient, heat resistance property upon moisture absorption, and electrical properties, a prepreg and single-layer or laminated sheet, a metal foil-clad laminate using the prepreg, and the like. The resin composition has polyphenylene ether (A) having a number average molecular weight of 500 to 5000, a phosphorus-containing cyanate ester compound (B) represented by formula (13), a cyclophosphazene compound (C), a halogen-free epoxy resin (D), a cyanate ester compound (E) other than the phosphorus-containing cyanate ester compound (B), an oligomer (F) of styrene and/or substituted styrene, and a filler (G), wherein a content of the phosphorus-containing cyanate ester compound (B) is 1 to 10 parts by mass based on 100 parts by mass of a total of the (A) to (F) components. wherein m represents an integer of 1 to 3.

Abstract: A resin composition has high flame retardancy and excellent heat resistance, peel strength with copper foil, thermal expansion coefficient, heat resistance property upon moisture absorption, and electrical properties, a prepreg and single-layer or laminated sheet, a metal foil-clad laminate using the prepreg, and the like. The resin composition has polyphenylene ether (A) having a number average molecular weight of 500 to 5000, a phosphorus-containing cyanate ester compound (B) represented by formula (13), a cyclophosphazene compound (C), a halogen-free epoxy resin (D), a cyanate ester compound (E) other than the phosphorus-containing cyanate ester compound (B), an oligomer (F) of styrene and/or substituted styrene, and a filler (G), wherein a content of the phosphorus-containing cyanate ester compound (B) is 1 to 10 parts by mass based on 100 parts by mass of a total of the (A) to (F) components. wherein m represents an integer of 1 to 3.

Abstract: A resin composition that can allow allowing a drying step after impregnation coating of a prepreg and lamination pressing performed at low temperatures in a short time and, at the same time, can maintain storage stability of the prepreg, comprises (A) an imidazole compound represented by formula (I), (B) an epoxy compound, and (C1) a cyanate compound or (C2) a BT resin. R1 and R2 represent an alkyl group, an alkenyl group an alkoxyl group, or a substituted or unsubstituted aromatic substituent; and R3 represents hydrogen, an alkyl group, an alkenyl group, an alkoxy group, a substituted or unsubstituted aromatic substituent, or a halogen group.