Abstract: There is proposed a powder application device P for producing blanks of thermoplastically deformable semifinished products for use as reinforcement elements, starting from a powder mixture containing a meltable plastics powder, comprising a downwardly open powder container B and a perforated stencil L, arranged beneath the latter and spaced apart therefrom, having one or more hole cutouts, said device being characterized in that the powder container B is rigidly connected to the perforated stencil L and is vertically lowerable as far as an auxiliary support or a distance of at most 5 mm therefrom, and is closable at its lower end by means of a horizontal closing plate S having a thickness slightly less than the distance between the powder container B and the perforated stencil L, wherein the closing plate S is movable in a horizontal plane such that it alternately closes and reopens the lower end of the powder container B.

Abstract: There is proposed a powder application device P for producing blanks of thermoplastically deformable semifinished products for use as reinforcement elements, starting from a powder mixture containing a meltable plastics powder, comprising a downwardly open powder container B and a perforated stencil L, arranged beneath the latter and spaced apart therefrom, having one or more hole cutouts, said device being characterized in that the powder container B is rigidly connected to the perforated stencil L and is vertically lowerable as far as an auxiliary support or a distance of at most 5 mm therefrom, and is closable at its lower end by means of a horizontal closing plate S having a thickness slightly less than the distance between the powder container B and the perforated stencil L, wherein the closing plate S is movable in a horizontal plane such that it alternately closes and reopens the lower end of the powder container B.

Abstract: The invention relates to a novel thermoplastic stiffening material used for manufacturing shoes or shoe parts, and to an environmentally friendly method for the production thereof. The inventive material is proved in the form of a hot-melt adhesive/filling compound and is characterized in that it is comprised of one or more hot-melt adhesives and of one or more fillers, which are provided in quantities ranging from 50 to 15% by weight and which do not dissolve in the hot-melt adhesive. The hot-melt adhesive/filler compound simultaneously fulfills the following parameters: 1. MVR value between 2 and 6, preferably between 3 and 5 cm3/10 min; 2. Surface tack, when measured according to DIN EN 14610 at 65° C., ranging from at least 10 N/2 cm, preferably 15 N/2 cm, particularly 20 N/2 cm; 3. Bonding value/peel resistance with regard to upper materials and linings of at least 30 N/5 cm when measured according to DIN 53357; 4.

Abstract: The invention relates to a novel thermoplastic stiffening material used for manufacturing shoes or shoe parts, and to an environmentally friendly method for the production thereof. The inventive material is provided in the form of a hot-melt adhesive/filler compound and is characterized in that it is comprised of one or more hot-melt adhesives and of one or more fillers, which are provided in quantities ranging from 50 to 15% by weight and which do not dissolve in the hot-melt adhesive. The hot-melt adhesive/filler compound simultaneously fulfills the following parameters: 1. MVR value between 2 and 6, preferably between 3 and 5 cm3/10 min; 2. Surface tack, when measured according to DIN EN 14610 at 65° C., ranging from at least 10 N/2 cm, preferably N/2 cm, particularly 20 N/2 cm; 3. Bonding value/peel resistance with regard to upper materials and linings of at least 30 N/5 cm when measured according to DIN 53357; 4.

Abstract: An aliphatic polyester amide which is hydrolysis-resistant includes a ternary polycondensation product of monomeric constituents composed of a monomeric constituent A which is at least one diol having a general formula: HO—R1—OH, where R1 is an aliphatic residue having 2-16 carbon atoms; a monomeric constituent B which is at least one dicarboxylic acid having a general formula: HOOC—R2—COOH, where R2 is an aliphatic residue having 1-14 carbon atoms; and a monomeric constituent C which is at least one diamine having a general formula: H2N—R3—NH2, where R3 is an aliphatic residue having 2-16 carbon atoms and is present in an amount of up to about 5% by weight based on total weight of the monomeric constituents, wherein polycondensation proceeds in the presence of a catalyst comprised of constituent D, which is a metal-containing catalyst, in combination with constituent E, which is at least one of an organic phosphorus compound and an inorganic phosphorus compound, and wherei

Abstract: The invention relates to a process for producing a three-dimensional stiffening element from a powder selected from the group consisting of a meltable plastic powder and a powder mixture comprising the meltable plastic powder comprising applying the powder to an auxiliary carrier in a template screen printing process with the aid of a template and subsequently transferring the thus obtained stiffening element to a substrate, the improvement comprising subsequent to the step of applying to the auxiliary carrier, compressing and sintering the powder with a hot molding plug to obtain a blank; lifting the plug while removing the blank from the auxiliary carrier and further melting the sintered plastic particles of the blank which are in contact with the molding plug; and said step of transferring comprising transferring the further melted blank onto the substrate disposed therebelow while lowering the molding plug.

Abstract: A stiffening material composed of 30 to 80 weight percent filler particles and 70 to 20 weight percent binder which is thermoplastically deformable and has melt-adhesive properties in the temperature range of 50.degree. to 80.degree. C., wherein the filler particles are plastic particles or particles having plastic surfaces with a particle size distribution of 50 to 500 microns.