Abstract: A method of manufacturing an electrochemical cell having a gel electrolyte. An electrochemical cell is provided having a cell casing, and a first electrode, a second electrode, an electrolyte solution and a temperature activated gelling agent disposed within the cell casing. A gel electrolyte comprising the electrolyte solution and the gelling agent is formed by passing a current through the electrochemical cell such that the temperature of the gelling agent exceeds the activation temperature of the gelling agent.

Abstract: A method of manufacturing an electrochemical cell having a gel electrolyte. An electrochemical cell is provided having a cell casing, and a first electrode, a second electrode, an electrolyte solution and a temperature activated gelling agent disposed within the cell casing. A gel electrolyte comprising the electrolyte solution and the gelling agent is formed by passing a current through the electrochemical cell such that the temperature of the gelling agent exceeds the activation temperature of the gelling agent.

Abstract: The invention relates to processes for the preparation of electrode compositions, especially those intended for use in supercapacitors. A process is provided for preparing lithium sulphite comprising the steps of:—a) introducing H2SO3 (aq) into a reaction vessel; b) reacting the H2SO3 (aq) with an aqueous suspension of Li2CO3 in the vessel to form an aqueous solution of Li2—CO3; and c) evaporating the solution to recover Li2CO3(s), wherein at least steps a) and b) are conducted under an inert atmosphere. Preferably, in step b) H2SO3 (aq) and Li2CO3 (aq) are reacted with each other in substantially equimolar amounts. There is also provided a process for forming an electrode material comprising a complexing step of causing lithium sulphite to form SO3 complexes at active N sites of a nitrogen-carbon structure, in the presence of a selected amount of a sink that absorbs the liberated lithium, so as to form the N:SO3 complexed electrode material.

Abstract: A method is provided for the synthesis of a mesoporous lithium transition metal compound, the method comprising the steps of (i) reacting a lithium salt with one or more transition metal salts in the presence of a surfactant, the surfactant being present in an amount sufficient to form a liquid crystal phase in the reaction mixture (ii) heating the reaction mixture so as to form a sol-gel and (iii) removing the surfactant to leave a mesoporous product. The mesoporous product can be an oxide, a phosphate, a borate or a silicate and optionally, an additional phosphate, borate or silicate reagent can be added at step (i). The reaction mixture can comprise an optional chelating agent and preferably, the reaction conditions at steps (i) and (ii) are controlled so as to prevent destabilization of the liquid crystal phase. The invention is particularly suitable for producing mesoporous lithium cobalt oxide and lithium iron phosphate.

Abstract: The invention relates to processes for the preparation of electrode compositions, especially those intended for use in supercapacitors. A process is provided for preparing lithium sulphite comprising the steps of:—a) introducing H2SO3 (aq) into a reaction vessel; b) reacting the H2SO3 (aq) with an aqueous suspension of Li2CO3 in the vessel to form an aqueous solution of Li2—CO3; and c) evaporating the solution to recover Li2CO3(s), wherein at least steps a) and b) are conducted under an inert atmosphere. Preferably, in step b) H2SO3 (aq) and Li2CO3 (aq) are reacted with each other in substantially equimolar amounts. There is also provided a process for forming an electrode material comprising a complexing step of causing lithium sulphite to form SO3 complexes at active N sites of a nitrogen-carbon structure, in the presence of a selected amount of a sink that absorbs the liberated lithium, so as to form the N:SO3 complexed electrode material.

Abstract: A method is provided for the synthesis of a mesoporous lithium transition metal compound, the method comprising the steps of (i) reacting a lithium salt with one or more transition metal salts in the presence of a surfactant, the surfactant being present in an amount sufficient to form a liquid crystal phase in the reaction mixture (ii) heating the reaction mixture so as to form a sol-gel and (iii) removing the surfactant to leave a mesoporous product. The mesoporous product can be an oxide, a phosphate, a borate or a silicate and optionally, an additional phosphate, borate or silicate reagent can be added at step (i). The reaction mixture can comprise an optional chelating agent and preferably, the reaction conditions at steps (i) and (ii) are controlled so as to prevent destabilisation of the liquid crystal phase. The invention is particularly suitable for producing mesoporous lithium cobalt oxide and lithium iron phosphate.