Abstract: Disclosed are graphite nanoplatelets produced by a process which comprises thermal plasma expansion of intercalated graphite to produce expanded graphite followed by exfoliation of the expanded graphite, where the exfoliation step is selected from ultrasonication, wet milling and controlled caviation and where greater than 95% of the graphite nanoplatelets have a thickness of from about 0.34 nm to about 50 nm and a length and width of from about 500 nm to about 50 microns. The intercalated graphite is intercalated for example with a mixture of sulfuric and nitric acids. The plasma reactor for example employs an RF induction plasma torch. All three exfoliation methods are performed in an organic solvent or water. The exfoliation steps may be performed with the aid of for example a nonionic surfactant. Also disclosed are plastic, ink, coating, lubricant or grease compositions comprising the graphite nanoplatelets.

Abstract: This invention relates to synthetically derived zinc phlogopite platelets, of superior aspect ratio, effect pigments comprising such synthetically derived platelets and methods of forming said platelets. More specifically the disclosure describes an improved hydrothermal synthesis of zinc phlogopite suitable as a platelets for interference pigments, barrier and flame retardant applications.

Abstract: This invention relates to synthetically derived zinc phlogopite substrates, of superior aspect ratio, effect pigments comprising such synthetically derived substrates and methods of forming said substrates. More specifically the disclosure describes an improved hydrothermal synthesis of zinc phlogopite suitable as a substrate for interference pigments, barrier and flame retardant applications.

Abstract: Disclosed are graphite nanoplatelets produced by a process which comprises thermal plasma expansion of intercalated graphite to produce expanded graphite followed by exfoliation of the expanded graphite, where the exfoliation step is selected from ultrasonication, wet milling and controlled caviation and where greater than 95% of the graphite nanoplatelets have a thickness of from about 0.34 nm to about 50 nm and a length and width of from about 500 nm to about 50 microns. The intercalated graphite is intercalated for example with a mixture of sulfuric and nitric acids. The plasma reactor for example employs an RF induction plasma torch. All three exfoliation methods are performed in an organic solvent or water. The exfoliation steps may be performed with the aid of for example a nonionic surfactant. Also disclosed are plastic, ink, coating, lubricant or grease compositions comprising the graphite nanoplatelets.