Abstract: An extruded matt foil has at least one layer in which glass beads are uniformly distributed in a polymer matrix with at least one fluoropolymer and at least one further layer. The matt foil has a particularly high UV-resistance, a high weathering resistance and excellent mechanical properties. Therefore, the foil is highly suitable for surface-protection of materials such as polyvinyl chloride (PVC) and for use in high-pressure laminates (HPLs).

Abstract: An extruded matt foil has at least one layer in which glass beads are uniformly distributed in a polymer matrix with at least one fluoropolymer and at least one further layer. The matt foil has a particularly high UV-resistance, a high weathering resistance and excellent mechanical properties. Therefore, the foil is highly suitable for surface-protection of materials such as polyvinyl chloride (PVC) and for use in high-pressure laminates (HPLs).

Abstract: The invention relates to novel composite materials with improved mechanical properties and improved weathering resistance, said composite materials being made of at least one material containing cellulose, preferably wood, and at least one plastic, and to a method for producing said composite materials and for using same.

Abstract: The invention relates to novel composite materials which are made of at least one material containing cellulose, preferably wood, and at least one plastic material, and which have improved mechanical and weather resistance properties.

Abstract: The invention relates to a multilayer film encompassing at least one upper layer a) and one middle layer b) composed of (meth)acrylate copolymers, and also a backing layer c) composed of polycarbonate, where the upper layer a) comprises a light stabilizer and is composed of a (meth)acrylate copolymer which can form semicompatible mixtures with the polycarbonate of the backing layer c), where a test specimen produced from a mixture composed of 20% by weight of (meth)acrylate copolymer and 80% by weight of polycarbonate has a tensile strain at break of at least 75% (ISO 527-2) at 23° C.

Abstract: The invention relates to a multilayered film comprising at least one upper layer a), a middle layer b) made of (meth)acrylate copolymer, and a supporting layer c) made of polycarbonate. Upper layer a) contains a light-stability agent and is made of a (meth)acrylate copolymer that, together with the polycarbonate of supporting layer c), can form partially compatible mixtures. A test piece, which is made from a mixture consisting of 20% by weight of (meth)acrylate copolymer and 80% by weight of polycarbonate, has a breaking elongation (ISO 527-2) of at least 75% at 23° C. The middle layer b) contains a colorant and, optionally, a light-stability agent and is made from an identical or different (meth)acrylate copolymer that, together with the polycarbonate of supporting layer c), can form partially compatible mixtures.

Abstract: The invention relates to a multilayer film encompassing at least one upper layer a) and one middle layer b) composed of (meth)acrylate copolymers, and also a backing layer c) composed of polycarbonate, where the upper layer a) comprises a light stabilizer and is composed of a (meth)acrylate copolymer which can form semicompatible mixtures with the polycarbonate of the backing layer c), where a test specimen produced from a mixture composed of 20% by weight of (meth)acrylate copolymer and 80% by weight of polycarbonate has a tensile strain at break of at least 75% (ISO 527-2) at 23° C.

Abstract: The invention relates to a polymer mixture, based on the (meth)acrylate (co)polymer components a.), b.), c.) and/or d.) according to claim 1, where a test specimen produced from the polymer mixture simultaneously has the following properties: a tensile modulus (ISO 527) of at least 2 500 MPa, a Vicat softening point VSP (ISO 306-350) of at least 110° C., an impact resistance (ISO 179-2D, flatwise) of at least 30 kJ/m2, and a melt index MVR (ISO 1133, 230° C./3.8 kg) of at least 1.0 cm3/10 at least The invention further relates to injection mouldings and to the use of the polymer mixture for production of injection mouldings.

Abstract: The invention relates to a polymer mixture based on the (meth)acrylate (co)polymer components a), b), c), and/or d) according to claim 1, where a test specimen produced from the polymer mixture simultaneously has the following properties: I. a tensile modulus (ISO 527) of at least 2600 MPa, II. a Vicat softening point VSP (ISO 306-B50) of at least 109° C., III. an impact strength (ISO 179-2D, flatwise) of at least 17 kJ/m2, and IV. a melt index MVR (ISO 1133, 230° C./3.8 kg) of at least 1.5 cm3/10 min. The invention further relates to injection mouldings and to the use of the polymer mixture for producing injection-moulded parts.

Abstract: The invention relates to a multilayered film comprising at least one upper layer a), a middle layer b) made of (meth)acrylate copolymer, and a supporting layer c) made of polycarbonate. Upper layer a) contains a light-stability agent and is made of a (meth)acrylate copolymer that, together with the polycarbonate of supporting layer c), can form partially compatible mixtures. A test piece, which is made from a mixture consisting of 20% by weight of (meth)acrylate copolymer and 80% by weight of polycarbonate, has a breaking elongation (ISO 527-2) of at least 75% at 23° C. The middle layer b) contains a colorant and, optionally, a light-stability agent and is made from an identical or different (meth)acrylate copolymer that, together with the polycarbonate of supporting layer c), can form partially compatible mixtures.

Abstract: The invention relates to a polymer mixture based on the (meth)acrylate (co)polymer components a), b), c), and/or d) according to claim 1, where a test specimen produced from the polymer mixture simultaneously has the following properties: I. a tensile modulus (ISO 527) of at least 2600 MPa, II. a Vicat softening point VSP (ISO 306-B50) of at least 109° C., III. an impact strength (ISO 179-2D, flatwise) of at least 17 kJ/m2, and IV. a melt index MVR (ISO 1133, 230° C./3.8 kg) of at least 1.5 cm3/10 min. The invention further relates to injection mouldings and to the use of the polymer mixture for producing injection-moulded parts.