Abstract: A hardener composition including: (a) a polymeric adduct; (b) a monomeric unmodified amine; and (c) an extender; a curable composition including (A) at least one epoxy compound; and (B) the above hardener composition; and a thermoset prepared from the above curable composition.

Abstract: A hardener composition comprising: a) an amine component; and b) a glycol ether component comprising i) from 10 weight percent to 70 weight percent alkylene glycol phenyl ether; ii) from 25 weight percent to 80 weight percent dialkylene glycol phenyl ether; iii) from 5 weight percent to 20 weight percent trialkylene glycol phenyl ether, is disclosed. The hardener composition can be used in epoxy thermoset formulations.

Abstract: A flooring coating composition includes a coating agent that is a reaction product of an epoxy based formulation, the epoxy based formulation being at least one of an epoxy prepolymer formulation, an epoxy-silane hybrid formulation, and an epoxy thiol acrylate formulation. The coating agent in a cured state exhibits a first tan delta peak between a first temperature range of 75 C to 0 C and a second tan delta peak between a second temperature range of 20 C and 75 C, according to a tan delta plot over a range of temperatures. A value of the first tan delta peak and a value of the second tan delta peak each represents a ratio of a loss modulus of the coating agent and a storage modulus of the coating agent at a specific temperature within the range of temperatures, as measured according to dynamic mechanical thermal analysis. The values of the first and the second tan delta peaks are from 0.10 to 0.80.

Abstract: A process comprising: a) producing a first adduct comprising a reaction product of a difunctional epoxy and Isophrondiamine (IPDA); b) producing a second adduct comprising a reaction product of a difunctional epoxy and m-Xylylenediamine (MXDA) and c) contacting i) the first adduct; ii) the second adduct; iii) an accelerator; and iv) a modifier to form a hardener composition, is disclosed. The hardener composition can be used with an epoxy compound to form a curable composition.

Abstract: A hardener composition comprising: a) an amine component; and b) a glycol ether component comprising i) from 10 weight percent to 70 weight percent alkylene glycol phenyl ether; ii) from 25 weight percent to 80 weight percent dialkylene glycol phenyl ether; iii) from 5 weight percent to 20 weight percent trialkylene glycol phenyl ether, is disclosed. The hardener composition can be used in epoxy thermoset formulations.

Abstract: Embodiments include curable compositions including a resin component and a hardener component. The resin component can include an epoxy compound that is selected from the group consisting of aromatic epoxy compounds, alicyclic epoxy compounds, aliphatic epoxy compounds, and combinations thereof, and a reactive diluent that includes a polymeric glycidyl ether. The hardener component can include an adduct and a Mannich base.

Abstract: There is provided a stable aqueous dispersion comprising (a) dispersed particles of one or more film-forming polymer that comprises 1% to 10% by weight, based on the solid weight of said polymer, of polymerized units of one or more functional monomer, wherein said functional monomer is selected from acid-functional monomers or amine-functional monomers or a mixture thereof, and (b) one or more multiglycidyl compound having 4 or more glycidyl groups per molecule.

Abstract: Embodiments include curable compositions including a resin component and a hardener component. The resin component can include an epoxy compound that is selected from the group consisting of aromatic epoxy compounds, alicyclic epoxy compounds, aliphatic epoxy compounds, and combinations thereof, and a reactive diluent that includes a polymeric glycidyl ether. The hardener component can include an adduct and a Mannich base.

Abstract: A coalescent composition including from 20 to 80% by weight, based on the weight of the coalescent composition, ethylene glycol phenyl ether and from 80% to 20% by weight, based on the weight of the coalescent composition, diethylene glycol phenyl ether and a coalescent composition including from 20 to 80% by weight, based on the weight of the coalescent composition, propylene glycol phenyl ether and from 80% to 20% by weight, based on the weight of the coalescent composition, dipropylene glycol phenyl ether are provided. An aqueous coating composition including the coalescent composition and a method for providing a coating are also provided.

Abstract: There is provided a stable aqueous dispersion comprising (a) dispersed particles of one or more film-forming polymer that comprises 1% to 10% by weight, based on the solid weight of said polymer, of polymerized units of one or more functional monomer, wherein said functional monomer is selected from acid-functional monomers or amine-functional monomers or a mixture thereof, and (b) one or more multiglycidyl compound having 4 or more glycidyl groups per molecule.

Abstract: A water-dispersible composition including a nanofiller-containing epoxy resin and a low temperature nonionic surfactant having a molecular weight of less than about 7,000 Daltons; and optionally an anionic surfactant or optionally a high temperature nonionic surfactant. The water-dispersible composition can be used to prepare an aqueous dispersion of the nanofiller-containing epoxy resin. The aqueous dispersion advantageously has a long shelf- stability. One method for preparing the aqueous dispersion includes using a high internal phase ratio emulsion process.

Abstract: A water-dispersible composition including a nanofiller-containing epoxy resin and a low temperature nonionic surfactant having a molecular weight of less than about 7,000 Daltons; and optionally an anionic surfactant or optionally a high temperature nonionic surfactant. The water-dispersible composition can be used to prepare an aqueous dispersion of the nanofiller-containing epoxy resin. The aqueous dispersion advantageously has a long shelf- stability. One method for preparing the aqueous dispersion includes using a high internal phase ratio emulsion process.