Abstract: A method for the synthesis of an oxide high-temperature superconductor of defined composition by sintering of the starting oxides, wherein sintering is effected in a chemically and phyically closed system by generating a preset oxygen partial pressure through the use of peroxide additives, and the oxidic starting mixture is chemically shielded against the container material and stabilized thermodynamically.

Abstract: Metallic implants with a coating of hydroxyl apatite are described. Hot isostatic pressing permits pore-free compaction of the hydroxyl apatite layer and results in firm bonding of the layer on the metallic core. The surface of the layer is partially dehydrated by means of ion bombardment, and a bioactive layer for osteogenesis is produced.

Abstract: A high-temperature and thermal-shock-resistant thermal insulating coating based upon flame- or plasma-sprayed ceramic materials. The coating consists of several layer sequences essentially of the same materials. Each layer sequence contains at least one ceramic and one cermet layer, and/or one ceramic and one metal layer, and/or one cermet and one metal layer.

Abstract: An implantable bone replacement material (body) based on completely or partially resorbable particles incorporated in a matrix material. The particles are composed of bioactive sintered calcium phosphate ceramic material having a CaO:P.sub.2 O.sub.5 composition ratio between 3:1 and 4:1. The replacement material (body) consists of a metal containing calcium phosphate ceramic material in the form of a monolayer of particles in the peripheral areas of the material (body) which serve as interfaces to the body tissue. The metal is compatible with body tissue. The ceramic particles have a size range between about 500 .mu.m and a few millimeters. The calcium phosphate particles are located so that they lie exposed on the upper surface of the material (body). Other embodiments and processes are also disclosed.

Abstract: A process for producing ceramic, ceramic-metal or metal catalyst supports or catalysts with open, interconnecting pores. The process forming a dense agglomeration of spherical, cylindrical or similar bodies of generally uniform size. These bodies are connected together at their mutual contact points, thereby producing a framework corresponding generally to the macropores and pore interconnections of the finished material in terms of size and arrangement. The framework is then filled with a suspension containing as solid components the catalyst support material and/or the catalyst material. The suspension can also contain a binding agent. The framework is subsequently dissolved away after at least the partial hardening of the cast mass without destroying the structure produced during hardening.