Abstract: The present invention relates to a molding composition comprising, by weight: a) 20% to 60% of at least one long-chain aliphatic polyamide having a number of carbon atoms per nitrogen atom of greater than or equal to 9, said at least one polyamide having an inherent viscosity in solution of less than or equal to 1.3, as determined in accordance with the standard ISO 307:2007 at a temperature of 20° C., b) 40% to 75% of glass fibers, and c) 0% to 5% by weight, by weight of at least one additive, the sum of the proportions of each constituent of said composition being equal to 100%, with the exclusion of an amorphous polyamide and a microcrystalline polyamide.

Abstract: A transparent molding composition including, by weight (with a total of 100%): (A) 35 to 84% of a polyamide mixture including: 10 to 95% by weight of at least one semi-crystalline aliphatic polyamide, whose average number of carbon atoms relative to nitrogen atoms is greater than or equal to 8; 90 to 5% by weight of at least one amorphous polyamide; (B) from over 10 to 30% of at least one impact modifier; (C) from 6 to 20% of short glass fibers; (D) 0 to 10% of at least one prepolymer; and (E) 0 to 5% of at least one additive selected from stabilizers, dyes, plasticizers, processing aids or a mixture thereof, the index of refraction of each constituent (A), (B), (C) and (D) being included between 1.500 and 1.540, and wherein said composition has no PEBA and has a dry-measured modulus at 23° C. over 1700 MPa.

Abstract: Molding composition, including by weight: (A) from 38 to 79.5% of at least one semi-crystalline aliphatic polyamide with the exclusion of PA6 and PA66, (B) from 10 to 20% of carbon fibres, (C) from 10 to 20% of hollow glass beads, (D) from 5.5 to 10% of at least one impact modifier having a flexural modulus of less than 200 MPa, in particular less than 100 MPa, as measured according to standard ISO 178: 2010, at 23° C., and (E) from 0.1 to 1% by weight of at least one additive, the sum of the proportions of each constituent (A)+(B)+(C)+(D)+(E) of the composition being equal to 100%.

Abstract: The invention relates to the use of at least one catalyst, at least one copper heat stabiliser and at least one oligo- or poly-carbodiimide with a matrix including at least one polyamide, in order to form a composition that has a good melt viscosity and is stable during transformation, in particular during extrusion.

Abstract: The use of at least one catalyst, at least one copper heat stabiliser and at least one oligo- or poly-carbodiimide with a matrix including at least one polyamide, in order to form a composition that has a good melt viscosity and is stable during transformation, in particular during extrusion.

Abstract: The present invention relates to the use of a composition comprising: 70 to 91% by weight of at least one semi-crystalline polyamide, 5 to 25% by weight of at least one polyolefin having an epoxy, anhydride or acid function introduced by grafting or copolymerisation, 3 to 20% by weight of at least one plasticizer, 0.05 to 5% by weight of at least one stabilizer on the basis of a copper complex, and at least one catalyst, said composition being free from alkaline metal halide and oligo- or polycarbodiimide, as sealing layer in a pipe containing oil or gas, the pipe being used in the exploitation of offshore oil or gas reservoirs.

Abstract: The invention relates to the use of at least one catalyst, at least one copper heat stabiliser and at least one oligo- or poly-carbodiimide with a matrix including at least one polyamide, in order to form a composition that has a good melt viscosity and is stable during transformation, in particular during extrusion.