Abstract: A preparation method of a ceramic membrane support is disclosed. Take aluminum hydroxide, produced through a carbon decomposing process by a sintering method, as a raw material, pre-sinter the aluminum hydroxide, and obtain a low-temperature alumina product A; add a first amount of mineralizer into the product A, grind after calcining the added product A, and obtain a ?-alumina product B; mix the product B with Al2O3.nH2O, calcine after adding a second amount of mineralizer into the mixed product B, and obtain a ?-alumina product C; grind, scatter and grade the calcined and heat-preserved ?-alumina product C, and obtain polyhedral alumina powders; mix the polyhedral alumina powders, water, humectant and dispersant and then sinter, and finally obtain the porous alumina support. The prepared support is easy to be sintered, is high in alumina purity, is good in corrosion resistance, and is improved in porosity and flux.

Abstract: A method for preparing a support of a molecular sieve membrane is provided and relates to a technical field of support preparation, including steps of: according to a molar ratio of magnesium, aluminum and silicon in cordierite, preparing a nanometer composite sol of magnesium, aluminum, silicon and lanthanum serving as a sintering aid through a sol-gel method, enveloping and bonding the sol on a surface of dispersed nano-sized cordierite powders, and transforming the sol into nanometer composite oxides through presintering; mixing the cordierite powders, a binder and water, forming mud, extruding the mud, forming the mud into a green body, and sintering the green body into a cordierite support; coating a layer of film on the cordierite support with an aqueous dispersant of zirconia, then sintering, and obtaining a support of a molecular sieve membrane, composited by a cordierite main support layer and a zirconia film layer.

Abstract: A preparation method of a ceramic membrane support is disclosed. Take aluminium hydroxide, produced through a carbon decomposing process by a sintering method, as a raw material, pre-sinter the aluminium hydroxide, and obtain a low-temperature alumina product A; add a first amount of mineralizer into the product A, grind after calcining the added product A, and obtain a ?-alumina product B; mix the product B with Al2O3.nH2O, calcine after adding a second amount of mineralizer into the mixed product B, and obtain a ?-alumina product C; grind, scatter and grade the calcined and heat-preserved ?-alumina product C, and obtain polyhedral alumina powders; mix the polyhedral alumina powders, water, humectant and dispersant and then sinter, and finally obtain the porous alumina support. The prepared support is easy to be sintered, is high in alumina purity, is good in corrosion resistance, and is improved in porosity and flux.

Abstract: A method for preparing a support of a molecular sieve membrane is provided and relates to a technical field of support preparation, including steps of: according to a molar ratio of magnesium, aluminum and silicon in cordierite, preparing a nanometer composite sol of magnesium, aluminum, silicon and lanthanum serving as a sintering aid through a sol-gel method, enveloping and bonding the sol on a surface of dispersed nano-sized cordierite powders, and transforming the sol into nanometer composite oxides through presintering; mixing the cordierite powders, a binder and water, forming mud, extruding the mud, forming the mud into a green body, and sintering the green body into a cordierite support; coating a layer of film on the cordierite support with an aqueous dispersant of zirconia, then sintering, and obtaining a support of a molecular sieve membrane, composited by a cordierite main support layer and a zirconia film layer.