Abstract: Disclosed is an injection stretch blow molded (ISBM) container containing a surface having a static coefficient of friction (COF) of 0.15 to 0.21, a dynamic COF of 0.06 to 0.1, wherein the surface retains a water contact angle of 76° or higher for up to three minutes after wetting of the surface with a water drop of 14 to 16 mm diameter and the container is made with a polymeric composition containing a high density polyethylene (HDPE) having a dispersity (Mw/Mn) of 9 or higher as measured by GPC; a MI2 of 1 g/10 min or higher as measured by ASTM D-1238; 190° C./2.16 kg, as measured by ASTM D-1238; and an environmental stress crack resistance (ESCR) at 100% Igepal of >150 hours as measured by ASTM D-1693, B.

Abstract: A catalyst component for olefin polymerization includes magnesium, titanium, a halogen, an internal electron donor compound, and a precipitation aid. The precipitation aid includes a precipitation aid represented by general formula (I). The precipitation aid represented by general formula (I) includes isomers represented by general formula (I-a) and/or (I-b).

Abstract: Disclosed is an injection stretch blow molded (ISBM) container containing a surface having a static coefficient of friction (COF) of 0.15 to 0.21, a dynamic COF of 0.06 to 0.1, wherein the surface retains a water contact angle of 76° or higher for up to three minutes after wetting of the surface with a water drop of 14 to 16 mm diameter and the container is made with a polymeric composition containing a high density polyethylene (HDPE) having a dispersity (Mw/Mn) of 9 or higher as measured by GPC; a MI2 of 1 g/10 min or higher as measured by ASTM D-1238; 190° C./2.16 kg, as measured by ASTM D-1238; and an environmental stress crack resistance (ESCR) at 100% Igepal of >150 hours as measured by ASTM D-1693, B.

Abstract: Disclosed are methods of additive manufacturing comprising polypropylene, and compositions created using the same.

Abstract: Processing parameters of polypropylene and/or polyethylene are adjusted by combining them with a non-fluorinated process aid. The process aid is an oleochemical derivative and/or a wax having a viscosity of from 10 cP to 100 cP. The wax is a branched ethylene-propylene copolymer. The processing parameter, e.g., pressure at the die, or volumetric output is adjusted for the polypropylene and/or polyethylene compared to the polypropylene and/or polyethylene without the non-fluorinated process aid at the same processing conditions. The mechanical properties of an extruded polymeric article including the non-fluorinated process aid are the same or are improved compared to the same composition without the non-fluorinated polymer processing aid or one that includes a fluorinated processing aid.

Abstract: A method of adjusting a processing parameter of a polymer is provided. The method has the steps a) and b). Step a) is combining polymer i) which is polypropylene and/or polyethylene with a process aid ii) to provide a polymer composition. Polymer i) has a peak molecular weight Mp and a polydispersity index PDI of 7 or higher. Step b) is processing the polymer composition at a processing condition. The processing parameter is adjusted at the processing condition for the polymer composition compared to a comparative polymer composition A); and a comparative polymer composition B). Comparative polymer composition A) lacks the process aid ii) but is otherwise identical to the polymer composition. Comparative polymer composition B) includes a comparative polymer having the same composition and Mp as polymer i) and a PDI less than polymer i) instead of the polymer i), but is otherwise identical to the polymer composition.

Abstract: A polymeric composition comprising at least 95 wt. % of a metallocene-catalyzed polypropylene, and at least one of a clarifying agent or a nucleating agent is disclosed. The polymeric composition can have a lower haze value when compared with a second polymeric composition that has the same components in the same wt. % amounts as the polymeric composition except that the polypropylene in the second polymeric composition is a Ziegler-Natta catalyzed polypropylene. The haze values can be determined by ASTM D1003 at a thickness of 50 mils.

Abstract: A polymeric composition is disclosed. The composition can include (a) at least 95 wt. % of a polypropylene, (b) a clarifying agent, and (c) a nucleating agent, wherein the presence of the clarifying agent and nucleating agent in the polymeric composition decreases the haze value, as determined by ASTM D1003 at a thickness of 40-80 mil, of the polymeric composition when compared with the haze value of the polymeric composition having the clarifying agent but not the nucleating agent.

Abstract: A method of making foamed styrenic copolymer comprising reacting the styrenic copolymer with an ionomer to form a composition; and contacting a blowing agent with the composition to form the foamed styrenic polymer. An article formed from a composition comprising a styrenic copolymer, an ionomer and a blowing agent.

Abstract: A polystyrene (PS) composition for making an extruded foam, the PS composition comprising: a dried PS/alumina compound comprising a PS and an alumina additive, wherein the dried PS/alumina compound has a moisture content, measured by Coulometer, that is less than or equal to about 0.05 weight percent (wt %); and a blowing agent.

Abstract: Disclosed is an injection stretch blow molded (ISBM) container containing a surface having a static coefficient of friction (COF) of 0.15 to 0.21, a dynamic COF of 0.06 to 0.1, wherein the surface retains a water contact angle of 76° or higher for up to three minutes after wetting of the surface with a water drop of 14 to 16 mm diameter and the container is made with a polymeric composition containing a high density polyethylene (HDPE) having a dispersity (Mw/Mn) of 9 or higher as measured by GPC; a MI2 of 1 g/10 min or higher as measured by ASTM D-1238; 190° C./2.16 kg, as measured by ASTM D-1238; and an environmental stress crack resistance (ESCR) at 100% Igepal of >150 hours as measured by ASTM D-1693, B.

Abstract: Thin polymer sheets and used thereof are described. A polymer sheet can include greater than 90 wt. % of a single-site catalyzed polyolefin (PO) and have a thickness of at least 0.0254 cm. The sheet can be used to produce molded articles.

Abstract: A polystyrene (PS) composition for making an extruded foam, the PS composition comprising polystyrene, a blowing agent, and an additive selected from glycerol monostearate (GMS), glycerol tri-stearate (GTS), mineral oil (MO), epoxidized soy oil (ESO), epoxidized polybutadiene, or combinations thereof. Methods of producing a low density polystyrene (PS) foam are also provided.

Abstract: The magnesium alkoxide particle contains the reaction product of the following components: 1) a magnesium powder; 2) a mixed alcohol; 3) a halogenating agent; and 4) a titanate compound. The magnesium alkoxide particle is used for preparing a catalyst for olefin polymerization.

Abstract: Disclosed is an extruded non-crosslinked polyethylene foam containing a metallocene polyethylene, a density of 0.35 g/cc or less, and a closed cell content higher than 70%, methods of making the extruded non-crosslinked polyethylene foam and articles containing the extruded non-crosslinked polyethylene foam.

Abstract: A method of producing a silane cross-linked polyethylene is disclosed which includes maleating a polyethylene polymer to form a maleated polyethylene and reacting the maleated polyethylene with a primary or secondary amino silane to form a silane-grafted polyethylene. The method further includes treating the silane-grafted polyethylene in a moisture curing process to form the silane cross-linked polyethylene.

Abstract: A catalyst component for olefin polymerization includes magnesium, titanium, a halogen, an internal electron donor compound, and a precipitation aid. The precipitation aid includes a precipitation aid represented by general formula (I). The precipitation aid represented by general formula (I) includes isomers represented by general formula (I-a) and/or (I-b).

Abstract: A polystyrene (PS) composition for making an extruded foam, the PS composition comprising: a dried PS/alumina compound comprising a PS and an alumina additive, wherein the dried PS/alumina compound has a moisture content, measured by Coulometer, that is less than or equal to about 0.05 weight percent (wt %); and a blowing agent.

Abstract: Polymer compositions and uses thereof are described. A polymeric composition can include a polyolefin polymer and a nucleating agent having an average particle size of less than 2 micrometers.

Abstract: A polymeric composition may include a polyolefin or styrenic polymer, a metallic acrylate salt, and an acid neutralizer.