Abstract: A preparation method of an alumina powder includes the following steps: subjecting the raw material powder having a particle size not exceeding 1,000 mesh to a shear treatment in the presence of a solvent and a polymerization inhibitor to obtain a stable suspension; mixing the suspension with a crystal plane growth guiding agent uniformly and subjecting the mixture to a hydrothermal treatment under a hermetic conditions, then performing a solid-liquid separation, and subjecting the solid to drying and roasting. The alumina powder contains alumina grains having a single-crystal structure and bas an approximate regular octahedral stereoscopic morphology. Eight sides of the alumina grain belong to the {111} family of crystal planes of ?-state alumina, and the grain size is 5-100 ?m.

Abstract: An alumina grain has a single-crystal structure and has an approximate regular octahedral stereoscopic morphology. Eight sides of the alumina grain belong to the {111} family of crystal planes of ?-state alumina, and the grain size is 5-100 ?m. The alumina grain is unique in crystal plane exposure and distribution, simple and feasible in preparation, and low in cost, and has higher operability, and thus has good application prospect in the field of catalysis and adsorption.

Abstract: The supporter material for catalyst includes a main body alumina and a rod-shaped alumina. The main body alumina is provided with micron-sized pore channels, at least part of the rod-shaped alumina is distributed on the exterior surface of the main body alumina and/or in the micron-sized pore channels with a pore diameter D within a range of 3-10 ?m; the rod-shaped alumina has a length of 1-12 ?m and a diameter of 80-300 nm. The alumina supporter material is used as a residual oil hydrogenation catalyst supporter to facilitate a long period operation of the residual oil hydrogenation, and has high demetalization rate, desulfurization rate and denitrification rate.

Abstract: The supporter material for catalyst includes a main body alumina and a rod-shaped alumina. The main body alumina is provided with micron-sized pore channels, at least part of the rod-shaped alumina is distributed on the exterior surface of the main body alumina and/or in the micron-sized pore channels with a pore diameter D within a range of 3-10 ?m; the rod-shaped alumina has a length of 1-12 ?m and a diameter of 80-300 nm. The alumina supporter material is used as a residual oil hydrogenation catalyst supporter to facilitate a long period operation of the residual oil hydrogenation, and has high demetalization rate, desulfurization rate and denitrification rate.

Abstract: The present invention provides a fibrous IM-5 molecular sieve and the preparation process thereof. According to the process according to the present invention, by adding an appropriate amount of a quaternary ammonium salt with a long carbon chain to the preparation system so as to occur a synergistic action with the organic templet agent, an IM-5 molecular sieve which would be otherwise a rodlike form is converted into the fibrous form. The IM-5 molecular sieve according to the present invention has an aspect ratio greater than that of the rodlike IM-5 molecular sieve obtained according to the prior art, such that the proportion of the exposed periphery crystal face is higher, which benefit to increasing the selectivity of the catalytic reaction for the corresponding crystal face.

Abstract: The present invention provides a hollow IM-5 molecular sieve sphere and the preparation process thereof. The process according to the present invention adds a relatively great amount of the surfactant of a cationic quaternary ammonium salt in the IM-5 molecular sieve system, to form a hollow IM-5 molecular sieve sphere via the micelle action by the surfactant, which structure benefits the mass transfer of the reaction process.

Abstract: The present invention provides a fibrous IM-5 molecular sieve and the preparation process thereof. According to the process according to the present invention, by adding an appropriate amount of a quaternary ammonium salt with a long carbon chain to the preparation system so as to occur a synergistic action with the organic templet agent, an IM-5 molecular sieve which would be otherwise a rodlike form is converted into the fibrous form. The IM-5 molecular sieve according to the present invention has an aspect ratio greater than that of the rodlike IM-5 molecular sieve obtained according to the prior art, such that the proportion of the exposed periphery crystal face is higher, which benefit to increasing the selectivity of the catalytic reaction for the corresponding crystal face.

Abstract: The present invention provides a hollow IM-5 molecular sieve sphere and the preparation process thereof. The process according to the present invention adds a relatively great amount of the surfactant of a cationic quaternary ammonium salt in the IM-5 molecular sieve system, to form a hollow IM-5 molecular sieve sphere via the micelle action by the surfactant, which structure benefits the mass transfer of the reaction process.