Abstract: The present invention produces a regular grain oriented electrical steel using a single cold reduction step having excellent and highly uniform magnetic quality. The method includes the steps of providing an electrical steel band having Mn of 0.024% or less in excess of that needed to combine with S and/or Se. The band is provided with an anneal at a temperature of from 900.degree.-1125.degree. C. (1650.degree.-2050.degree. F.) for a time up to 10 minutes and slowly cooled to 480.degree.-650.degree. C. (900.degree.-1200.degree. F.) followed by rapid cooling to a temperature below 100.degree. C. (212.degree. F.). The annealed band must have a critical amount of austenite, .gamma..sub.1150.degree. C., of 7% or more. The annealed band is cold reduced in a single stage to the desired final thickness. The strip is decarburized and provided with an annealing separator coating on one or more surfaces of the strip.