Abstract: A process is provided for preparing a polyester styrene vinyl hybrid polymer latex composition which may be used to prepare toner for use in electrographic applications by the emulsion aggregation process. The process includes preparing a polyester by polycondensation, preparing a solution of the polyester in a mixture of styrene and vinyl monomers, emulsifying the polyester/monomer solution, and polymerizing the emulsion via emulsion polymerization to yield a polyester styrene vinyl hybrid polymer latex composition. The latex affords excellent fixing when used in chemically produced toner made by the emulsion aggregation process.

Abstract: A process is provided for preparing a bimodal styrene vinyl polymer latex composition, which may be used to prepare toner for use in electrophotographic applications by the emulsion aggregation process. The process includes preparing a low molecular weight styrene polymer (LMWP) by solution polymerization, preparing a solution of the LMWP in a mixture of styrene and vinyl monomers, emulsifying the LMWP/monomer solution in water, and polymerizing the LMWP and mixture of styrene and vinyl monomers via emulsion polymerization to yield a bimodal molecular weight composition. The latex affords excellent fixing when used in chemically produced toners such as toners produced by emulsion aggregation.

Abstract: A bimodal, crosslinked toner resin can be prepared in non-aqueous solvent, e.g., toluene, using standard solution polymerization techniques. The resin-forming process prepares a precursor resin from ethylenically unsaturated monomer(s), and then grafts maleic anhydride onto the precursor resin to form a modified precursor resin. The modified precursor resin is reacted with a polyfunctional molecule, e.g. a diol, to provide a crosslinked resin. The process is preferably conducted in the presence of a low molecular weight polymeric additive, e.g., polystyrene, to provide a bimodal as well as crosslinked toner resin composition. With the addition of a colorant, a toner powder may be formed.

Abstract: A bimodal, crosslinked toner resin can be prepared in non-aqueous solvent, e.g., toluene, using standard solution polymerization techniques. The resin-forming process prepares a precursor resin from ethylenically unsaturated monomer(s), and then grafts maleic anhydride onto the precursor resin to form a modified precursor resin. The modified precursor resin is reacted with a polyfunctional molecule, e.g. a diol, to provide a crosslinked resin. The process is preferably conducted in the presence of a low molecular weight polymeric additive, e.g., polystyrene, to provide a bimodal as well as crosslinked toner resin composition. With the addition of a colorant, a toner powder may be formed.

Abstract: Disclosed is a toner composition useful for electrophotography consisting of (1) the reaction product of a polyfunctional azide and a cross-linkable toner resin that is a copolymer of a styrene material and an acrylate or methacrylate, or a polyester resin that is the reaction product of a dicarboxylic acid and a dihydric alcohol, and (2) a colorant.