Abstract: The present invention provides a composition for use in forming an enamel cover coat from which baked-on foods can be removed without the need for pyrolysis or highly alkaline cleaners. The enamel cover coat preferably exhibits no chipping or other surface defects subsequent to a 2.0 mm Plum Jam Test and an acid resistance of A or better according to ISO 2722. The composition according to the invention includes a glass component including at least a first glass frit comprising a low SiO2 glass frit. Preferably, the glass component includes a blend of the first glass frit and at least a second glass frit. Preferably, the first glass frit includes by weight from about 30% to about 45% P2O5, from about 20% to about 40% Al2O3, from about 15% to about 35% Li2O+Na2O+K2O, up to about 15% B2O3, up to about 15% MgO+CaO+SrO+BaO+ZnO, up to about 10% TiO2+ZrO2, and up to about 10% SiO2.

Abstract: The present invention provides a composition for use in forming an enamel cover coat from which baked-on foods can be removed without the need for pyrolysis or highly alkaline cleaners. The enamel cover coat preferably exhibits no chipping or other surface defects subsequent to a 2.0 mm Plum Jam Test and an acid resistance of A or better according to ISO 2722. The composition according to the invention includes a glass component including at least a first glass frit comprising a low SiO2 glass frit. Preferably, the glass component includes a blend of the first glass frit and at least a second glass frit. Preferably, the first glass frit includes by weight from about 30% to about 45% P2O5, from about 20% to about 40% Al2O3, from about 15% to about 35% Li2O+Na2O+K2O, up to about 15% B2O3, up to about 15% MgO+CaO+SrO+BaO+ZnO, up to about 10% TiO2+ZrO2, and up to about 10% SiO2.

Abstract: The present invention provides a composition for use in forming an opaque porcelain enamel coating on a metal substrate. A porcelain enamel coating formed using a composition according to the invention readily adheres to metal substrates such as, for example, steel, that are degreased-only. Furthermore, such a porcelain enamel coating displays an acid resistance of A according to ISO 2722 and good easy-to-clean properties. The composition according to the invention includes a glass component including by weight from about 45% to about 55% SiO2, from about 8% to about 17% B2O3, from about 1.8% to about 17.7% SrO+BaO, from about 1.9% to about 10% Li2O, up to about 6% ZrO2, from about 2% to about 11% TiO2, from about 1.5% to about 6% K2O, from about 1% to about 4% MoO3, from about 0.3% to about 13% Na2O, up to about 2% NiO, up to about 3% Al2O3, up to about 2.9% MnO, up to about 0.8% CoO, up to about 3% MgO, up to about 5% CaO, and up to about 2% Sb2O3.